Achieving ultra-high strength in Be/Al composites by self-exhaust pressure infiltration and hot extrusion process

被引:13
作者
Kuang, Zeyang [1 ]
Yang, Wenshu [1 ,3 ]
Ju, Boyu [1 ]
Xia, Yixiao [1 ]
Wang, Zhijun [1 ]
Gong, Deng [1 ]
Fu, Linlin [1 ]
Wu, Yiming [1 ]
Sun, Dongli [1 ]
Wu, Gaohui [1 ,2 ]
机构
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
[2] Harbin Inst Technol, Sch Mat Sci & Engn, Key Lab Adv Struct Funct Integrated Mat & Green Mf, Harbin 150001, Peoples R China
[3] Harbin Inst Technol, Sch Mat Sci & Engn, PO 3023,Sci Pk,2 Yikuang St, Harbin 150080, Peoples R China
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2023年 / 862卷
基金
中国博士后科学基金; 中国国家自然科学基金;
关键词
Self -exhaust pressure infiltration; Metal matrix composites (MMC); Be; Al; Microstructure; Mechanical properties; ALUMINUM-MATRIX COMPOSITES; MECHANICAL-PROPERTIES; INTERFACIAL REACTIONS; FATIGUE BEHAVIOR; MICROSTRUCTURE; BERYLLIUM; TENSILE; DEFORMATION; TEMPERATURE; FRACTURE;
D O I
10.1016/j.msea.2022.144473
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Beryllium particle reinforced aluminum matrix (Be/Al) composite with exceptionally high strength was fabri-cated from Be debris by self-exhaust pressure infiltration and hot extrusion process. The microstructures char-acteristics and mechanical properties of the Be/Al composite at as-cast and as-extruded state were systematically investigated in the current study. It was found for the as-cast composite that uniform distribution of beryllium particles with average size of 2.2 mu m were achieved, the microcracks in beryllium particles were repaired in situ by infiltrating liquid aluminum into these microcracks under external pressure. The Be phase and Al phase were well bonded despite the presence of nano BeO at the interface. After hot extrusion, the beryllium particle deformed and elongated along the extrusion direction. The average grain size of Al was refined from hundreds of microns to 450 nm, and the dislocation density increased significantly. The tensile strength and yield strength of Be/Al composite reached 595 MPa and 494 MPa by hot extrusion, respectively. The ultra-high strength was mainly related to grain boundaries strengthening, dislocation strengthening, precipitation strengthening and load transfer strengthening. Compared with the composites prepared by the investment casting and powder metallurgy methods, the Be/Al composite showed more than 100% increment in strengthening efficiency and 80% increment in yield strength. It indicated that the self-exhaust pressure infiltration technology combined with hot extrusion process was a feasible and successful method to prepare high performance Be/Al composites.
引用
收藏
页数:13
相关论文
共 52 条
[21]   The influence of particle size and particle fracture on the elastic/plastic deformation of metal matrix composites [J].
Nan, CW ;
Clarke, DR .
ACTA MATERIALIA, 1996, 44 (09) :3801-3811
[22]   ASSESSMENT OF MODELS USED TO PREDICT THE STRENGTH OF DISCONTINUOUS SILICON-CARBIDE REINFORCED ALUMINUM-ALLOYS [J].
NARDONE, VC .
SCRIPTA METALLURGICA, 1987, 21 (10) :1313-1318
[23]   Evaluation of the tensile and fatigue behaviour of ingot metallurgy beryllium/aluminium alloys [J].
Nardone, VC ;
Garosshen, TJ .
JOURNAL OF MATERIALS SCIENCE, 1997, 32 (15) :3975-3985
[24]   Evaluation of the tensile and fatigue behaviour of a powder metallurgy beryllium/aluminium alloy [J].
Nardone, VC ;
Garosshen, TJ .
JOURNAL OF MATERIALS SCIENCE, 1997, 32 (10) :2549-2557
[25]   ON THE STRENGTH OF DISCONTINUOUS SILICON-CARBIDE REINFORCED ALUMINUM COMPOSITES [J].
NARDONE, VC ;
PREWO, KM .
SCRIPTA METALLURGICA, 1986, 20 (01) :43-48
[26]   On the mechanisms associated with the chemical reactivity of Be in steam [J].
Petti, DA ;
Smolik, GR ;
Anderl, RA .
JOURNAL OF NUCLEAR MATERIALS, 2000, 283 :1390-1395
[27]   Pitting corrosion of cast metallurgy aluminum-beryllium alloys in sulfuric acid solutions [J].
Prater, W. L. .
CORROSION, 2008, 64 (06) :517-531
[28]  
Ramnath BV, 2014, REV ADV MATER SCI, V38, P55
[29]  
Schuster G, 2013, Light Metals., V2016, P259
[30]   A COMBINED MICROSTRUCTURE STRENGTHENING ANALYSIS OF SICP/AL METAL-MATRIX COMPOSITES [J].
SEKINE, H ;
CHEN, R .
COMPOSITES, 1995, 26 (03) :183-188