Covalent organic frameworks based hierarchical porous hybrid monolithic capillary: Synthesis, characterization, and applications in trace metals analysis

The preparation of hierarchical porous monolithic column with high covalent organic frameworks (COF) loading and micropores accessibility is challenging due to the easy aggregability and sedimentation of COFs. Herein, a novel strategy based on high internal phase emulsion (HIPE) polymerization was proposed for preparing COF hybrid capillary monolithic column with hierarchical porosity. COFs with different frameworks including imine COFs (COF-OMe, COF-F and COF-SH), triazine COF (CTF-1) and boron-based COF (COF-5) were selected to investigate the universality of the preparation strategy. The presence of COF in the monolithic capillary was confirmed by scanning electron microscope, X-ray diffraction and fourier transform infrared spectroscopy. Nitrogen adsorption/desorption experiments and thermogravimetric analysis showed that the prepared COF hybrid monolithic capillary exhibited high COF loading (e.g., 28.7% for COF-SH) and accessibility (e.g., 98.5% for COFSH), mainly due to the thin walls of void-window structures originated from polymerization of HIPE. The successful preparation of water-stable COF-F, COF-OMe, COF-SH and CTF-1 hybrid monolithic columns demonstrated the proposed synthesis strategy is universal to water-stable COF without tedious optimization of dispersion system, effectively avoiding the sedimentation of COF in pre-polymerization solution. Then, the sulfhydryl-modified COF hybrid polymer (poly(COF-SH-HIPE)) monolithic column was evaluated for the extraction of heavy metal ions, and a method based on poly(COF-SH-HIPE) monolithic capillary microextraction on-line coupled with inductively coupled plasma mass spectrometry detection was developed for analysis of trace Cd, Hg and Pb in human fluid samples.