Enhancement of Crack Resistance of Phthalonitrile-Based Carbon Fiber Reinforced Plastics by Introducing Polyamide Nonwoven Materials

被引:4
作者
Kutovaya, I. V. [1 ]
Poliakova, D. I. [1 ]
Erdni-Goryaev, E. M. [1 ]
Lipatov, Ya. V. [1 ]
Afanaseva, E. S. [1 ]
Morozov, O. S. [1 ]
Babkin, A. V. [1 ]
Kepman, A. V. [1 ]
机构
[1] Moscow MV Lomonosov State Univ, Fac Chem, Moscow 119991, Russia
关键词
MECHANICAL-PROPERTIES; CURE REACTION; RESINS; COMPOSITES; BEHAVIOR; POLYMERIZATION; TRANSITION; MATRICES;
D O I
10.1134/S1560090423600171
中图分类号
O63 [高分子化学(高聚物)];
学科分类号
070305 ; 080501 ; 081704 ;
摘要
The effect of introduction of polyamide nonwoven materials on the thermal and mechanical properties of polymer composite materials based on phthalonitriles and a carbon fabric is studied. It is shown that the addition of 3 wt % of polyamide nonwoven material causes a 44% increase in the specific work of delamination. At room temperature elastic mechanical characteristics, such as compressive strength and compressive modulus, for the composite modified with the nonwoven material increase by 12 and 100%, respectively. According to dynamic mechanical analysis, upon reaching 169 degrees C the melting of polyamide occurs; however, there remains the possibility to use the composites above this temperature, as confirmed by mechanical tests performed at 200 degrees C.
引用
收藏
页码:672 / 680
页数:9
相关论文
共 56 条
[1]   High performance carbon-carbon composites obtained by a two-step process from phthalonitrile matrix composites [J].
Aleshkevich, Vladislav V. ;
Bulgakov, Boris A. ;
Lipatov, Yakov, V ;
Babkin, Aleksandr, V ;
Kepman, Alexey, V .
MENDELEEV COMMUNICATIONS, 2022, 32 (03) :327-330
[2]   End-functionalized thermoplastic-toughened phthalonitrile composites: influence on cure reaction and mechanical and thermal properties [J].
Augustine, Dhanya ;
Mathew, Dona ;
Nair, C. P. Reghunadhan .
POLYMER INTERNATIONAL, 2015, 64 (01) :146-153
[3]   Phenol-containing phthalonitrile polymers - synthesis, cure characteristics and laminate properties [J].
Augustine, Dhanya ;
Mathew, Dona ;
Nair, C. P. Reghunadhan .
POLYMER INTERNATIONAL, 2013, 62 (07) :1068-1076
[4]   Mechanical and thermal properties of modified bismaleimide matrices toughened by polyetherimides and polyimide [J].
Babkin, Alexander V. ;
Erdni-Goryaev, Erdni M. ;
Solopchenko, Alexander V. ;
Kepman, Alexey V. ;
Avdeev, Viktor V. .
POLYMERS FOR ADVANCED TECHNOLOGIES, 2016, 27 (06) :774-780
[5]   Bisphthalonitrile-based Thermosets as Heat-resistant Matrices for Fiber Reinforced Plastics [J].
Bulgakov, B. A. ;
Morozov, O. S. ;
Timoshkin, I. A. ;
Babkin, A. V. ;
Kepman, A. V. .
POLYMER SCIENCE SERIES C, 2021, 63 (01) :64-101
[6]   Phthalonitrile-carbon fiber composites produced by vacuum infusion process [J].
Bulgakov, B. A. ;
Sulimov, A. V. ;
Babkin, A. V. ;
Timoshkin, I. A. ;
Solopchenko, A. V. ;
Kepman, A. V. ;
Avdeev, V. V. .
JOURNAL OF COMPOSITE MATERIALS, 2017, 51 (30) :4157-4164
[7]   Dual-curing thermosetting monomer containing both propargyl ether and phthalonitrile groups [J].
Bulgakov, B. A. ;
Sulimov, A. V. ;
Babkin, A. V. ;
Kepman, A. V. ;
Malakho, A. P. ;
Avdeev, V. V. .
JOURNAL OF APPLIED POLYMER SCIENCE, 2017, 134 (18)
[8]   Carbon fabric reinforced propargyl ether/phthalonitrile composites produced by vacuum infusion [J].
Bulgakov, Boris A. ;
Belsky, Kirill S. ;
Nechausov, Sergey S. ;
Afanaseva, Ekaterina S. ;
Babkin, Alexander V. ;
Kepman, Alexey V. ;
Avdeev, Viktor V. .
MENDELEEV COMMUNICATIONS, 2018, 28 (01) :44-46
[9]   Flame-retardant carbon fiber reinforced phthalonitrile composite for high-temperature applications obtained by resin transfer molding [J].
Bulgakov, Boris A. ;
Sulimov, Artem V. ;
Babkin, Alexander V. ;
Afanasiev, Dmitry V. ;
Solopchenko, Alexander V. ;
Afanaseva, Ekaterina S. ;
Kepman, Alexey V. ;
Avdeev, Viktor V. .
MENDELEEV COMMUNICATIONS, 2017, 27 (03) :257-259
[10]   Effect of poly(ether ether ketone) and allyl compounds on microstructure and properties of bismaleimide [J].
Chen, Yufei ;
Guo, Hongyuan ;
Geng, Chengbao ;
Wu, Yunzhong ;
Dai, Guoqing ;
Teng, Chengjun .
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS, 2019, 30 (02) :991-1000