The dominant role of defects on fatigue behaviour of a SLM Ni-based superalloy at elevated temperature

被引：22
|
作者：
Wang, M. L. [1 ]
Yang, X. G. [1 ]
Li, B. [1 ]
Shi, D. Q. [1 ]
Miao, G. L. [2 ]
Guo, S. Q. [2 ]
Fan, Y. S. [3 ,4 ]
机构：
[1] Beihang Univ, Sch Energy & Power Engn, Beijing 102206, Peoples R China
[2] Chengdu Holy Grp Ind Co Ltd, Chengdu 610041, Sichuan, Peoples R China
[3] Beihang Univ, Res Inst Aeroengine, Beijing 102206, Peoples R China
[4] Beihang Univ, Natl Key Lab Sci & Technol Aeroengine Aerothermody, Beijing 102206, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 176卷
基金：
中国博士后科学基金; 中国国家自然科学基金;
关键词：
Selective laser melting; Fatigue life scatter; Additive manufacturing defects; Critical defect characterization; Ni-based superalloy; LOW-CYCLE FATIGUE; X-RAY MICROTOMOGRAPHY; MECHANICAL-PROPERTIES; SURFACE-ROUGHNESS; VOID GROWTH; STRENGTH PREDICTION; SCANNING STRATEGY; CRACK INITIATION; LIFE PREDICTION; LASER;
D O I：
10.1016/j.ijfatigue.2023.107894
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This research investigates the impact of defects on the fatigue properties of a selective laser melted Ni-based superalloy at elevated temperatures. Results show that 78.6% of the fatigue failures are initiated by defects, with a larger scatter in fatigue life at lower stress levels. And the coalescence and growth of defects are captured by X-ray computed tomography (XCT). Besides, a quantitative analysis indicates that the fatigue life increases with defect location but decreases with defect size, which is influenced by defect shape. A modified stress intensity range, & UDelta;KL, is proposed, considering the effect of the three factors. Statistical characterization shows larger extreme values for critical defects compared to XCT observation.
引用
收藏
页数：18
相关论文
共 50 条
  • [1] Experimental investigation on low cycle fatigue and fracture behaviour of a notched Ni-based superalloy at elevated temperature
    Yuan, S. H.
    Wang, Y. R.
    Wei, D. S.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2014, 37 (09) : 1002 - 1012
  • [2] The effects of microstructure and temperature on the deformation heterogeneities and fatigue behaviour of a Ni-based superalloy
    Rai, R. K.
    Paulose, N.
    Sahu, J. K.
    PHILOSOPHICAL MAGAZINE, 2024, 104 (11-12) : 537 - 556
  • [3] Competing fatigue failure behaviors of Ni-based superalloy FGH96 at elevated temperature
    Miao, Guolei
    Yang, Xiaoguang
    Shi, Duoqi
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 668 : 66 - 72
  • [4] Investigation of impact toughness of a Ni-based superalloy at elevated temperature
    Yang, Y. H.
    Yu, J. J.
    Sun, X. F.
    Jin, T.
    Guan, H. R.
    Hu, Z. Q.
    MATERIALS & DESIGN, 2012, 36 : 699 - 704
  • [5] Anisotropy in flow behaviour of directionally solidified Ni-based superalloy under compression at an elevated temperature
    Gupta, Richa
    Prasad, M. J. N. V.
    Pant, Prita
    MATERIALIA, 2023, 32
  • [6] Effect of defects and hydrogen on the fatigue limit of Ni-based superalloy 718
    Kevinsanny
    Okazaki, Saburo
    Takakuwa, Osamu
    Ogawa, Yuhei
    Okita, Koichi
    Funakoshi, Yusuke
    Yamabe, Junichiro
    Matsuoka, Saburo
    Matsunaga, Hisao
    FATIGUE DESIGN 2019, INTERNATIONAL CONFERENCE ON FATIGUE DESIGN, 8TH EDITION, 2019, 19 : 312 - 319
  • [7] The role of cyclic oxidation on low cycle fatigue crack initiation and growth behaviour of a Ni-based superalloy
    Rai, R. K.
    MATERIALS CHEMISTRY AND PHYSICS, 2025, 332
  • [8] EFFECT OF CRYSTALLOGRAPHIC PROPERTIES ON LOW CYCLE FATIGUE STRENGTH AT ELEVATED TEMPERATURE FOR NI-BASED DIRECTIONALLY SOLIDIFIED SUPERALLOY
    Yokoyama, Takashi
    Sekihara, Masaru
    PROCEEDINGS OF THE ASME TURBO EXPO: TURBINE TECHNICAL CONFERENCE AND EXPOSITION, 2014, VOL 7A, 2014,
  • [9] Effect of defects on the fatigue limit of Ni-based superalloy 718 with different grain sizes
    Kevinsanny
    Okazaki, Saburo
    Takakuwa, Osamu
    Ogawa, Yuhei
    Okita, Koichi
    Funakoshi, Yusuke
    Yamabe, Junichiro
    Matsuoka, Saburo
    Matsunaga, Hisao
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (05) : 1203 - 1213
  • [10] Low-cycle fatigue behaviour of a Ni-based single-crystal superalloy
    Segersall, Mikael
    Moverare, Johan J.
    Leidermark, Daniel
    Simonsson, Kjell
    11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 416 - 421
12345