The influence of Ca2+ on the growth mechanism of corrosion product film on N80 steel in CO2 corrosion environments

被引：12
|
作者：
Ren, Xiedong [1 ]
Lu, Yuan [2 ]
Wei, Qiang [2 ]
Yu, Liusi [3 ]
Zhai, Kaiyuan [1 ]
Tang, Jiayi [1 ]
Wang, Hu [1 ,3 ]
Xie, Juan [1 ]
机构：
[1] Southwest Petr Univ, Sch New Energy & Mat, Chengdu 610500, Peoples R China
[2] CenerTech Oilfield Chem Co Ltd, CNOOC, Tianjin 300450, Peoples R China
[3] Mat Corros & Protect Key Lab Sichuan Prov, Zigong, Peoples R China
来源：
CORROSION SCIENCE | 2023年 / 218卷
关键词：
CO2; corrosion; Iron carbonate; Calcium carbonate; EIS; SEM; CARBON-STEEL; INTERNAL CORROSION; PITTING CORROSION; GAS-PRODUCTION; OIL; PIPELINES; CALCIUM; TEMPERATURE; TRANSPORT; BEHAVIOR;
D O I：
10.1016/j.corsci.2023.111168
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The influence of Ca2+ on the growth mechanism of CO2 corrosion products was investigated by weight loss, in situ electrochemical measurements and analysis of corrosion products. With the increase of Ca2+ concentration in solution, the crystallinity of product film, FexCa(1-x)CO(3), weakened and gradually turned to amorphous structure, which provided less protectiveness and elevated the corrosion rate. The high concentration of Ca2+ resulted in the "unstable" growth of FexCa1-_xCO3. At 10000 mg L-1 Ca2+, complicated FexCa1_xCO(3) structures with different Ca content formed. The linear relation between Ca2+ concentration in solution and molar fraction of Ca in the film was also proposed.
引用
收藏
页数：16
相关论文
共 50 条
  • [1] Role of Ca2+ in the CO2 corrosion behavior and film characteristics of N80 steel and electroless Ni-P coating at high temperature and high pressure
    Li, Jiankuan
    Sun, Chong
    Roostaei, Morteza
    Mahmoudi, Mahdi
    Fattahpour, Vahidoddin
    Zeng, Hongbo
    Luo, Jing-Li
    MATERIALS CHEMISTRY AND PHYSICS, 2021, 267
  • [2] Influence of CO2 partial pressure and flow rate on the corrosion behavior of N80 steel in 3.5% NaCl
    Chen, Xuezhong
    Yang, Xiaomin
    Zeng, Mingyou
    Wang, Hu
    INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2023, 18 (08):
  • [3] Corrosion Behavior of N80 Steel in Underground Supercritical CO2 Environments
    Ma, Guoliang
    CHEMISTRY AND TECHNOLOGY OF FUELS AND OILS, 2024, 60 (02) : 491 - 500
  • [4] Interaction of silty sand and preformed corrosion products on N80 carbon steel in CO2 environment
    Chen, Longjun
    Liu, Wei
    Zhang, Tianyi
    Dong, Baojun
    Li, Hai
    Sun, Yipu
    Fan, Yueming
    Zhao, Yonggang
    Li, Wenqi
    CORROSION SCIENCE, 2022, 205
  • [5] The role of Ca2+ ions on Ca/Fe carbonate products on X65 carbon steel in CO2 corrosion environments at 80 and 150 °C
    Shamsa, Amir
    Barker, Richard
    Hua, Yong
    Barmatov, Evgeny
    Hughes, Trevor L.
    Neville, Anne
    CORROSION SCIENCE, 2019, 156 : 58 - 70
  • [6] Crevice corrosion of N80 carbon steel in CO2-saturated environment containing acetic acid
    Li, Y. Z.
    Xu, N.
    Liu, G. R.
    Guo, X. P.
    Zhang, G. A.
    CORROSION SCIENCE, 2016, 112 : 426 - 437
  • [7] N80 Oil Tube Steel Corrosion Behavior in Different CO2 Saturated Brine
    Ma, Yun
    Zhang, Qingbo
    Bai, Haitao
    EKOLOJI, 2018, 27 (106): : 113 - 121
  • [8] Galvanic corrosion between N80 carbon steel and 13Cr stainless steel under supercritical CO2 conditions
    Li, Y. Y.
    Wang, Z. Z.
    Guo, X. P.
    Zhang, G. A.
    CORROSION SCIENCE, 2019, 147 : 260 - 272
  • [9] Corrosion behaviour of N80 carbon steel in formation water under dynamic supercritical CO2 condition
    Zhang, G. A.
    Liu, D.
    Li, Y. Z.
    Guo, X. P.
    CORROSION SCIENCE, 2017, 120 : 107 - 120
  • [10] The Impact of Temperature on CO2 Corrosion and the Formation of Corrosion Product Film
    Zhai, Kaiyuan
    Guo, Liang
    Zhu, Ning
    Tang, Jiayi
    Yu, Liusi
    Wang, Hu
    Xie, Juan
    CORROSION, 2024, 80 (06) : 589 - 602
12345