Synthesis, densification, and cation inversion in high entropy (Co,Cu,Mg,Ni,Zn)Al2O4 spinel

The synthesis, densification behavior, and crystallographic site occupancy were investigated for four different spinel-based ceramics, including a high-entropy spinel (Co0.2Cu0.2Mg0.2Ni0.2 Zn-0.2)Al2O4. Each composition was reacted to form a single phase, but analysis of X-ray diffraction patterns revealed differences in cation site occupancy with the high-entropy spinel being nearly fully normal. Densification behavior was investigated and showed that fully dense ceramics could be produced by hot pressing at temperatures as low as 1375 & DEG;C for all compositions. Vickers' hardness values were at least 10 GPa for all compositions. The cations present in the high-entropy spinel appear to have a stabilizing effect that led to nearly normal site occupancy compared to full cation inversion behavior of nickel aluminate spinel. This is the first report that compares cation site occupancy of a high-entropy spinel to conventional spinel ceramics.