TRIBOLOGICAL AND MECHANICAL PROPERTIES OF NANOCRYSTALLINE TiN, TiAlN, AND TiSiN PVD COATINGS

被引：6
作者：
Duan, L. L. [1 ]
Yang, G. Y. [1 ]
Hao, D. C. [1 ]
Huang, F. [2 ]
Xing, J. [1 ]
Liu, K. X. [1 ]
机构：
[1] Northeast Elect Power Univ, 169 Changchun Rd, Jilin, Jilin, Peoples R China
[2] Jilin Railway Technol Coll, Jilin, Jilin, Peoples R China
来源：
STRENGTH OF MATERIALS | 2023年 / 55卷 / 04期
关键词：
multiarc ion plating; strengthening mechanism; mechanical properties; friction; wear; MICROSTRUCTURE; SI; NANOCOMPOSITES; TEMPERATURE; HARDNESS; ORIGIN; FILMS; ZR;
D O I：
10.1007/s11223-023-00573-w
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
TiN, TiAlN, and TiSiN coatings were deposited on the W6Mo5Cr4V2 steel substrate by hollow cathodic-assisted multiarc ion plating technology. The tribological properties of these coatings are comparatively studied. The microstructure, element composition, nanomechanics, and wear properties of the substrate and coating surface of high-speed steel were evaluated by XRD, SEM, EDS, TEM, XPS, and nanoindentation tests. The results show that the mechanical properties of ternary coating TiAlN and TiSiN are improved compared with high-speed steel and binary TiN coatings, with TiAlN hardness and elastic modulus of 44.8 and 438.6 GPa and TiSiN hardness and elastic modulus of 34.8 and 333.2 GPa. The TiAlN coating has the strongest ability to resist plastic deformation due to solid solution strengthening. TiSiN can improve the plasticity and toughness of hard coatings after fine-grain strengthening. A strong positive correlation exists between the amount of sample wear and the H-3/E*(2) value. The surface friction coefficients of TiN, TiAlN, and TiSiN were all small compared with high-speed steel, and the roughness at the wear tracks of high-speed steel increased while the roughness at the wear tracks of the coating samples decreased.
引用
收藏
页码：822 / 833
页数：12
相关论文
共 26 条
[11]   Self-propagating high-temperature synthesis of advanced materials and coatings [J].
Levashov, E. A. ;
Mukasyan, A. S. ;
Rogachev, A. S. ;
Shtansky, D. V. .
INTERNATIONAL MATERIALS REVIEWS, 2017, 62 (04) :203-239
[12]   Characterization and corrosion behaviors of TiN/TiAlN multilayer coatings by ion source enhanced hybrid arc ion plating [J].
Li, Gui ;
Zhang, Lin ;
Cai, Fei ;
Yang, Ying ;
Wang, Qimin ;
Zhang, Shihong .
SURFACE & COATINGS TECHNOLOGY, 2019, 366 :355-365
[13]   Nanohardness and tribological properties of nc-TiB2 coatings [J].
Lofaj, F. ;
Moskalewicz, T. ;
Cempura, G. ;
Mikula, M. ;
Dusza, J. ;
Czyrska-Filemonowicz, A. .
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2013, 33 (12) :2347-2353
[14]   A comparative study of analytical thermal models to predict the orthogonal cutting temperature of AISI 1045 steel [J].
Ning, Jinqiang ;
Liang, Steven Y. .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2019, 102 (9-12) :3109-3119
[15]   Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology [J].
Oliver, WC ;
Pharr, GM .
JOURNAL OF MATERIALS RESEARCH, 2004, 19 (01) :3-20
[16]   Effect of Thermal Annealing in Vacuum and in Air on Nanograin Sizes in Hard and Superhard Coatings Zr-Ti-Si-N [J].
Pogrebnjak, A. D. ;
Shpak, A. P. ;
Beresnev, V. M. ;
Kolesnikov, D. A. ;
Kunitskii, Yu A. ;
Sobol, O. V. ;
Uglov, V. V. ;
Komarov, F. F. ;
Shypylenko, A. P. ;
Makhmudov, N. A. ;
Demyanenko, A. A. ;
Baidak, V. S. ;
Grudnitskii, V. V. .
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2012, 12 (12) :9213-9219
[17]   Influence of deposition temperature on microstructure formation of Ti-Al-C-N ceramic coatings prepared via pulsed-DC PACVD [J].
Rashidi, Mahshid ;
Tamizifar, Morteza ;
Boutorabi, Seyyed Mohammad Ali .
SURFACE & COATINGS TECHNOLOGY, 2021, 407
[18]   Mechanical and tribological properties of Ti-Al-Ta-N/TiAl and Ti-Al-Ta-N/Ta multilayer coatings deposited by DC magnetron sputtering [J].
Shugurov, A. R. ;
Kuzminov, E. D. .
SURFACE & COATINGS TECHNOLOGY, 2022, 441
[19]   Fabrication and characterization of in-situ duplex plasma-treated nanocrystalline Ti/AlTiN coatings [J].
Tan, Chaolin ;
Kuang, Tongchun ;
Zhou, Kesong ;
Zhu, Hongmei ;
Deng, Yang ;
Li, Xueping ;
Cai, Panpan ;
Liu, Zongwen .
CERAMICS INTERNATIONAL, 2016, 42 (09) :10793-10800
[20]   Microstructure and mechanical properties of functionally gradient cemented carbides fabricated by microwave heating nitriding sintering [J].
Tang, Siwen ;
Liu, Deshun ;
Li, Pengnan ;
Jiang, Lingli ;
Liu, Wenhui ;
Chen, Yuqiang ;
Niu, Qiulin .
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2016, 58 :137-142
123