Influences of Fe Content and Cold Drawing Strain on the Microstructure and Properties of Powder Metallurgy Cu-Fe Alloy Wire

被引:9
作者
Yuan, Xiaobo [1 ]
Zhang, Ping [1 ]
Wang, Jianxiang [1 ]
Yang, Biaobiao [1 ,2 ,3 ]
Li, Yunping [1 ]
机构
[1] Cent South Univ, State Key Lab Powder Met, Changsha 410083, Peoples R China
[2] IMDEA Mat Inst, C Eric Kandel 2, Getafe 28906, Spain
[3] Univ Politecn Madrid, Dept Mat Sci, ETS Ingenieros Caminos, Madrid 28040, Spain
关键词
Cu-Fe wire; powder metallurgy; cold drawing; ultimate tensile strength; electrical conductivity; Fe phase; ELECTRICAL-CONDUCTIVITY; STRENGTH; DEFORMATION; EVOLUTION; PRECIPITATION; NUCLEATION; MECHANISMS; COPPER;
D O I
10.3390/ma16145180
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
To study the effects of Fe content and cold drawing strain on the microstructure and properties, Cu-Fe alloys were prepared via powder metallurgy and hot extrusion. Scanning electron microscopy was applied to observe the Fe phase, and the ultimate tensile strength was investigated using a universal material testing machine. Alloying with an Fe content below 10 wt.% formed a spherically dispersed Fe phase via the conventional nucleation and growth mechanism, whereas a higher Fe content formed a water-droplet-like Fe phase via the spinodal decomposition mechanism in the as-extruded Cu-Fe alloy. Further cold drawing induced the fiber structure of the Fe phase (fiber strengthening), which could not be destroyed by subsequent annealing. As the Fe content increased, the strength increased but the electrical conductivity decreased; as the cold drawing strain increased, both the strength and the electrical conductivity roughly increased, but the elongation roughly decreased. After thermal-mechanical processing, the electrical conductivity and strength of the Cu-40Fe alloy could reach 51% IACS and 1.14 GPa, respectively. This study can provide insight into the design of high-performance Cu-Fe alloys by tailoring the size and morphology of the Fe phase.
引用
收藏
页数:13
相关论文
共 42 条
[1]   Microstructure and strength of Cu-Fe in situ composites after very high drawing strains [J].
Biselli, C ;
Morris, DG .
ACTA MATERIALIA, 1996, 44 (02) :493-504
[2]   Intragranular nucleation of tetrahedral precipitates and discontinuous precipitation in Cu-5wt%Ag [J].
Bonvalet, M. ;
Sauvage, X. ;
Blavette, D. .
ACTA MATERIALIA, 2019, 164 :454-463
[3]   ON SPINODAL DECOMPOSITION [J].
CAHN, JW .
ACTA METALLURGICA, 1961, 9 (09) :795-801
[4]   Kinetics of secondary phase precipitation during spinodal decomposition in duplex stainless steels: A kinetic Monte Carlo model - Comparison with atom probe tomography experiments [J].
Emo, Jonathan ;
Pareige, Cristelle ;
Saillet, Sebastien ;
Domain, Christophe ;
Pareige, Philippe .
JOURNAL OF NUCLEAR MATERIALS, 2014, 451 (1-3) :361-365
[5]   Effect of Ag on the microstructure and properties of Cu-Fe in situ composites [J].
Gao, HY ;
Wang, J ;
Shu, D ;
Sun, BD .
SCRIPTA MATERIALIA, 2005, 53 (10) :1105-1109
[6]   Combined Fe and O effects on microstructural evolution and strengthening in Cu-Fe nanocrystalline alloys [J].
Guo, Jinming ;
Shao, Qinqin ;
Renk, Oliver ;
Li, Lei ;
He, Yunbin ;
Zhang, Zaoli ;
Pippan, Reinhard .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 772
[7]   Hall-Petch relation and boundary strengthening [J].
Hansen, N .
SCRIPTA MATERIALIA, 2004, 51 (08) :801-806
[8]   Thermo-mechanical processing and properties of Cu-9Fe-1.2Co microcomposite wires [J].
Hong, SI ;
Song, JS ;
Kim, HS .
SCRIPTA MATERIALIA, 2001, 45 (11) :1295-1300
[9]   Microstructure and Properties of a Novel Cu-Ni-Co-Si-Mg Alloy with Super-high Strength and Conductivity [J].
Huang, Jiazhen ;
Xiao, Zhu ;
Dai, Jie ;
Li, Zhou ;
Jiang, Hongyun ;
Wang, Wei ;
Zhang, Xiaoxuan .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 744 :754-763