Combining pre-rolling with retrogression and re-aging treatment to balance strength and corrosion resistance of 7A99 Al alloy

被引：7
作者：
Zhang, Tao [1 ]
Hou, Yu-zhu [2 ]
Que, Biao-hua [2 ]
Tian, Yu-xin [3 ]
Chen, Liang [2 ]
机构：
[1] Nanjing Vocat Univ Ind Technol, Sch Mech Engn, Nanjing 210023, Peoples R China
[2] Shandong Univ, Minist Educ, Key Lab Liquid Solid Struct Evolut & Proc Mat, Jinan 250061, Peoples R China
[3] Shandong Technol & Business Univ, Sch Comp Sci & Technol, Yantai 264005, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2023年 / 33卷 / 10期
关键词：
aging; pre-rolling; precipitates; mechanical properties; corrosion resistance; ZN-MG ALLOY; ALUMINUM-ALLOYS; CRACKING BEHAVIOR; MICROSTRUCTURE; CU; PRECIPITATION; PREDEFORMATION; MODEL;
D O I：
10.1016/S1003-6326(23)66307-1
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The 7A99 Al alloy was subjected to peak aging (PA) and retrogression + re-aging (RRA), and the pre-rolling (R) was combined with RRA (RRRA) to balance the mechanical properties and corrosion resistance. The results show that the precipitates of PA-treated sample are mainly unstable eta' phase with small size, while the coarse and stable eta phase appears after RRA and RRRA. The grain boundary precipitates of PA-treated sample exhibit the smallest size and continuous distribution, while they show increased size, discontinuous distribution, and Cu enrichment after RRA and RRRA. The hardness and strength of RRRA-treated sample are higher than those of RRA-treated one, and they are even close to the values of PA-treated one. Moreover, the samples exhibit better corrosion resistance after RRA and RRRA than that after PA. These results indicate that the proposed RRRA method can enhance the corrosion resistance without a significant sacrifice on the mechanical strength.
引用
收藏
页码：2913 / 2925
页数：13
相关论文
共 42 条
  • [31] Effects of Retrogression and Re-aging Treatment on Microstructures and Mechanical Properties of Ultrahigh Strength Al-Zn-Mg-Cu-Zr Alloy Containing Sc
    Li Wenbin
    Pan Qinglin
    Liu Junsheng
    Liang Wenjie
    Liu Xiaoyan
    He Yunbin
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (09) : 1646 - 1650
  • [32] Assessment of Retrogression and Re-aging Treatment on Microstructural and Mechanical Properties of AL-Zn-Mg-Cu P/M Alloy
    Naeem, Haider T.
    Mohammad, Kahtan S.
    Hussin, Kamarudin
    Tan, T. Qing
    Idris, M. Sobri
    INTERNATIONAL CONFERENCE ON MATHEMATICS, ENGINEERING AND INDUSTRIAL APPLICATIONS 2014 (ICOMEIA 2014), 2015, 1660
  • [33] Retrogression and re-aging treatment of Al-9.99%Zn-1.72%Cu-2.5%Mg-0.13%Zr aluminum alloy
    冯春
    刘志义
    宁爱林
    刘延斌
    曾苏民
    Transactions of Nonferrous Metals Society of China, 2006, (05) : 1163 - 1170
  • [34] Retrogression and re-aging treatment of Al-9.99%Zn-1.72%Cu-2.5%Mg-0.13%Zr aluminum alloy
    Feng Chun
    Liu Zhi-yi
    Ning Ai-lin
    Liu Yan-bin
    Zeng Su-min
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 (05) : 1163 - 1170
  • [35] Effect of non-isothermal retrogression and re-aging treatment on microstructure evolution and mechanical properties of Al-Zn-Mg-Cu alloy
    Yang, Wenhao
    Zhang, Yelin
    Yang, Hongfu
    Zhang, Liu
    Zheng, Shanju
    Li, Mengnie
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 31 : 1728 - 1743
  • [36] Simultaneously improving the strength and ductility of an Ag-free 2195 Al-Li alloy by T8 treatment with cryogenic pre-rolling
    Dai, Wen
    Jiang, Yong
    Yao, Jiangang
    Wang, Yiren
    Cao, Fuhua
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 976
  • [37] Synchronous improvement of mechanical properties and stress corrosion resistance by stress-aging coupled with natural aging pre-treatment in an Al-Zn-Mg alloy with high recrystallization fraction
    Zhang, D.
    Jiang, H. C.
    Cui, Z. J.
    Yan, D. S.
    Song, Y. Y.
    Rong, L. J.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2022, 121 : 40 - 51
  • [38] Concurrent Improvement of strength, formability and SCC resistance of Al-Zn-Mg-Cu alloy by hot stamping after rapid heating and re-aging on paint baking treatment
    Shoichi, Hirosawa
    Junmo, Kim
    Tomoyoshi, Maeno
    Yasushi, Suzuki
    Yuuji, Yabuki
    20TH METAL FORMING INTERNATIONAL CONFERENCE, METAL FORMING 2024, 2024, 44 : 227 - 232
  • [39] Non-isothermal aging: A heat treatment method that simultaneously improves the mechanical properties and corrosion resistance of ultra-high strength Al-Zn-Mg-Cu alloy
    Wang, Weiyi
    Pan, Qinglin
    Wang, Xiangdong
    Sun, Yuanwei
    Ye, Ji
    Lin, Geng
    Liu, Shuhui
    Huang, Zhiqi
    Xiang, Shengqian
    Wang, Xiaoping
    Liu, Yaru
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 845
  • [40] Effects of pre-strain and aging treatments on the mechanical property and corrosion resistance of the spray formed ultra-high strength Al-Zn-Mg-Cu alloy
    Wang, Xiangdong
    Pan, Qinglin
    Wang, Weiyi
    Huang, Zhiqi
    Chen, Jian
    Pan, Baiqing
    Liu, Xiong
    MATERIALS CHARACTERIZATION, 2022, 194
12345