Influence of accelerated corrosion on bi-material steel-CFRP double-lap joints bonded with thick adhesive

被引:2
|
作者
Jaiswal, Pankaj R. [1 ]
Kumar, Rahul Iyer [1 ]
Rooms, Koen [1 ]
Rousseau, Joren [1 ]
Pondicherry, Kannaki [1 ]
De Waele, Wim [1 ]
机构
[1] Univ Ghent, Dept Electromech Syst & Met Engn EMSME, Soete Lab, B-9050 Ghent, Belgium
关键词
Bi-material; adhesive joints; electrochemical corrosion; shear strength; ENVIRONMENTAL DURABILITY; GALVANIC CORROSION; FRP/STEEL JOINTS; CARBON; PERFORMANCE; STRENGTH; BEHAVIOR; TEMPERATURE; PLATES;
D O I
10.1177/09544089221105850
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Bi-material steel-composite joints attract interest for marine applications. The marine environment imposes corrosion which is a prolonged process. This work presents a two-electrode electrochemical setup for accelerating free corrosion of the steel surfaces of bi-material joints. It is used to study the impact of accelerated corrosion on the mechanical performance of bi-material double lap specimens subjected to quasi-static tensile testing. Several test series have been conducted to evaluate the influence of overlap length and bond line thickness on shear strength and failure mode. Sixty specimens with a thick layer of methyl methacrylate adhesive have been fabricated and cured at room temperature for at least 24 h. Subsequently, 30 specimens were aged by subjecting them to electrochemical corrosion for 24 h. All specimens were tested for failure in quasi-static tensile loading while monitoring the strain fields in the joint area using digital image correlation. The measurements reveal a homogeneous shear strain field at the onset of loading, with a rapidly increasing shear strain concentration near the edges of the bond line preceding final failure. Both a decrease in the adhesive thickness and an increase in the overlap length increase the shear strength. Higher shear strength was observed for the electrochemically aged specimens than that of non-aged specimens. This is attributed to the faster residual curing of the adhesive during ageing because an increasing percentage of copper ions (released from the anode) accelerates the curing of the MMA adhesive. The electrochemically aged specimens showed mixed failure modes, i.e. cohesive failure and adhesive failure at the interface between steel and adhesive, and skin failure within the composite laminates.
引用
收藏
页码:38 / 51
页数:14
相关论文
共 44 条
  • [31] Durability of CFRP-Steel Double-Lap Joints under Cyclic Freeze-Thaw/Wet-Dry Conditions
    Ren, Xiang
    Jiang, Lingzhi
    He, Jun
    Yang, Yi
    Sun, Yamin
    Liu, Qunfeng
    Chen, Shaojie
    POLYMERS, 2022, 14 (17)
  • [32] Analytical investigation of thermal and mechanical load effects on stress distribution in adhesive layer of double-lap metal-composite bonded joints
    Kumazawa, Hisashi
    Kasahara, Toshiyuki
    ADVANCED COMPOSITE MATERIALS, 2019, 28 (04) : 425 - 444
  • [33] Stress redistributions in adhesively bonded double-lap joints, with elastic-perfectly plastic adhesive behavior, subjected to axial lap-shear cyclic loading
    Markolefas, S. I.
    Papathanassiou, Th. K.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2009, 29 (07) : 737 - 744
  • [34] Fatigue damage and life evaluation of thick bi-material double strap joints for use in marine applications
    Kumar, Rahul Iyer
    Jaiswal, Pankaj
    De Waele, Wim
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (07) : 2099 - 2111
  • [35] Mixed-mode I plus II fatigue/fracture characterisation of bi-material Aluminium/CFRP bonded joints
    Moreira, R. D. F.
    de Moura, M. F. S. F.
    Silva, F. G. A.
    Reina, J. P. A.
    COMPOSITES PART B-ENGINEERING, 2022, 246
  • [36] Durability of CFRP strengthened steel plate double-strap joints in accelerated corrosion environments
    Batuwitage, Chamila
    Fawzia, Sabrina
    Thambiratnam, David
    Al-Mahaidi, Riadh
    COMPOSITE STRUCTURES, 2017, 160 : 1287 - 1298
  • [37] Effect of functionalized nano-SiO2 addition on bond behavior of adhesively bonded CFRP-steel double-lap joint
    Li, You
    Li, Chuanxi
    He, Jun
    Gao, Youwei
    Hu, Zheng
    CONSTRUCTION AND BUILDING MATERIALS, 2020, 244
  • [38] Investigation of Residual Strength in CFRP Double-Adhesive Single Lap Bonded Joints after Low-velocity Impact
    Han, Shanling
    Yuan, Fengjie
    Wang, Tao
    Li, Zhiyong
    Li, Yong
    Journal of Adhesion, 2024,
  • [39] Investigation of Residual Strength in CFRP Double-Adhesive Single Lap Bonded Joints after Low-velocity Impact
    Han, Shanling
    Yuan, Fengjie
    Wang, Tao
    Li, Zhiyong
    Li, Yong
    JOURNAL OF ADHESION, 2024,
  • [40] Fracture characterization of a bi-material bonded aluminum/CFRP joints under mixed-mode I plus II loading
    Moreira, Raul D. F.
    de Moura, Marcelo F. S. F.
    Silva, Filipe G. A.
    Rodrigues, Jhonny S.
    Silva, Fernando D. R.
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (08) : 2215 - 2226