Influence of accelerated corrosion on bi-material steel-CFRP double-lap joints bonded with thick adhesive

被引:2
|
作者
Jaiswal, Pankaj R. [1 ]
Kumar, Rahul Iyer [1 ]
Rooms, Koen [1 ]
Rousseau, Joren [1 ]
Pondicherry, Kannaki [1 ]
De Waele, Wim [1 ]
机构
[1] Univ Ghent, Dept Electromech Syst & Met Engn EMSME, Soete Lab, B-9050 Ghent, Belgium
关键词
Bi-material; adhesive joints; electrochemical corrosion; shear strength; ENVIRONMENTAL DURABILITY; GALVANIC CORROSION; FRP/STEEL JOINTS; CARBON; PERFORMANCE; STRENGTH; BEHAVIOR; TEMPERATURE; PLATES;
D O I
10.1177/09544089221105850
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Bi-material steel-composite joints attract interest for marine applications. The marine environment imposes corrosion which is a prolonged process. This work presents a two-electrode electrochemical setup for accelerating free corrosion of the steel surfaces of bi-material joints. It is used to study the impact of accelerated corrosion on the mechanical performance of bi-material double lap specimens subjected to quasi-static tensile testing. Several test series have been conducted to evaluate the influence of overlap length and bond line thickness on shear strength and failure mode. Sixty specimens with a thick layer of methyl methacrylate adhesive have been fabricated and cured at room temperature for at least 24 h. Subsequently, 30 specimens were aged by subjecting them to electrochemical corrosion for 24 h. All specimens were tested for failure in quasi-static tensile loading while monitoring the strain fields in the joint area using digital image correlation. The measurements reveal a homogeneous shear strain field at the onset of loading, with a rapidly increasing shear strain concentration near the edges of the bond line preceding final failure. Both a decrease in the adhesive thickness and an increase in the overlap length increase the shear strength. Higher shear strength was observed for the electrochemically aged specimens than that of non-aged specimens. This is attributed to the faster residual curing of the adhesive during ageing because an increasing percentage of copper ions (released from the anode) accelerates the curing of the MMA adhesive. The electrochemically aged specimens showed mixed failure modes, i.e. cohesive failure and adhesive failure at the interface between steel and adhesive, and skin failure within the composite laminates.
引用
收藏
页码:38 / 51
页数:14
相关论文
共 44 条
  • [1] Stress analysis of double-lap bi-material joints bonded with thick adhesive
    Saleh, Mohamed Nasr
    Saeedifar, Milad
    Zarouchas, Dimitrios
    De Freitas, Sofia Teixeira
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2020, 97
  • [2] ADHESIVE INFLUENCE ON DOUBLE-LAP BONDED-JOINTS ASSEMBLIES
    Nemes, Ovidiu
    STUDIA UNIVERSITATIS BABES-BOLYAI CHEMIA, 2010, 55 (02): : 389 - 394
  • [3] EFFECTIVENESS OF ADHESIVE CFRP/STEEL JOINTS - DOUBLE-LAP STATIC TESTS
    Kaluza, Marta
    Hulimka, Jacek
    Kubica, Jan
    BRITTLE MATRIX COMPOSITES 11, 2015, : 479 - 488
  • [4] Damage characterization of CFRP /steel double-lap bonded joints based on AE and DIC
    Zhang, Zhiyuan
    Xu, Changhang
    Xie, Jing
    Sun, Xueying
    Wang, Wenao
    Li, Na
    COMPOSITE STRUCTURES, 2024, 346
  • [5] Double-lap adhesive bonded-joints assemblies modeling
    Nemes, O.
    Lachaud, F.
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2010, 30 (05) : 288 - 297
  • [6] Adhesive influence modeling on double-lap joints assemblies
    Nemes, Ovidiu
    STUDIA UNIVERSITATIS BABES-BOLYAI CHEMIA, 2007, 52 (04): : 175 - 181
  • [7] BOND SHEAR-STRENGTH FOR ADHESIVE-BONDED DOUBLE-LAP JOINTS
    TONG, LY
    INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 1994, 31 (21) : 2919 - 2931
  • [8] APPROXIMATE SOLUTION OF DOUBLE-LAP ADHESIVE-BONDED JOINTS BY MEANS OF ASYMPTOTIC EXPANSIONS
    GILIBERT, Y
    RIGOLOT, A
    COMPTES RENDUS HEBDOMADAIRES DES SEANCES DE L ACADEMIE DES SCIENCES SERIE B, 1979, 288 (23): : 387 - 390
  • [9] MICROCRACK INITIATION IN ADHESIVE BONDED DOUBLE-LAP JOINTS WITH SCARFED ENDS OF OUTER ADHERENDS
    GILIBERT, Y
    KLEIN, MLL
    JOURNAL OF ADHESION, 1989, 28 (01): : 51 - 69
  • [10] A bi-material property based FE modelling method for progressive damage analyses of composite double-lap bolted joints
    Shan, Meijuan
    Liu, Fengrui
    Fang, Ziang
    Zhao, Libin
    Zhang, Jianyu
    RESULTS IN PHYSICS, 2018, 11 : 674 - 683