Low-Temperature In Situ Lithiation Construction of a Lithiophilic Particle-Selective Interlayer for Solid-State Lithium Metal Batteries

Unexpected interface resistance and lithium dendrite puncture hinder the application of garnet-type solid-state electrolytes in high-energy-density systems. Different from the previous high-temperature (>180 C-degrees) molten lithium that promotes the alloying reaction between the coating layer and Li to enhance the interface contact, herein, we introduce liquid-metal-like SbCl3 to construct a three-dimensional Li+ directional-selection interlayer by in situ low-temperature lithiation (80 C-degrees). An interlayer with a more negative interface energy composed of SbLi3 and LiCl exhibits a superior affinity with Li and LGLZO, which reduces the interface resistance and suppresses the growth of Li dendrites by an insulated electron. The introduction of the SbCl3 modification layer into Li/Li symmetric cells enables charge/discharge at a current density of 6.0 mA cm(-2) and operation for more than 1000 h under 2.0 mA cm(-2 )at room temperature. The full cells with the LiFePO4 cathode exhibit a high residual capacity of 144.8 mAh g(-1) at 0.5 C after 1000 cycles and excellent cycling stability with a retention ratio of 94.7% at 1 C after 600 cycles. The low-temperature lithiation method based on an energy-saving perspective should be applied to other types of solid-state electrolyte modification strategies.