Twisted Poly(p-terphenyl-co-m-terphenyl)-Based Anion Exchange Membrane for Water Electrolysis

In order to improve the mechanical and water electrolysis performance of anion exchange membranes (AEMs), we adjusted the ratio between p-terphenyl and m-terphenyl to balance the backbone conformation, which gives it a better suitability for a better combination with cations. The results showed that poly(m-terphenyl-co-p-terphenyl)-based AEMs have excellent mechanical properties. Among them, the m-p-TP-40-BOP-ASU membrane has the highest tensile strength and elongation at break (75.72 MPa and 16.07%). The ionic conductivity reaches 137.14 mS cm(-1) at 80 degrees C owing to the fact that efficient ion-conducting channels are formed by well-balanced molecular structures. The current density of the m-p-TP-40-BOP-ASU membrane reached 1.96 A cm(-2) (1 M KOH aq, 2.0 V and 60 degrees C). After testing for 112 h under a current density of 500 mA cm(-2), the voltage increased by 102 mV compared to the initial electrolysis voltage. All results have shown that m-p-TP-x-BOP-ASU has excellent electrolysis performance and electrochemical durability and has a promising application prospect in AEM water electrolyzers.