Phase equilibria in the YbCl2-MCl (M = Li, Na, K) binary systems

被引：1

作者：

Chojnacka, Ida ^{[1
]}

Rycerz, L. ^{[1
]}

Kapala, J. ^{[1
]}

Gaune-Escard, M. ^{[2
]}

Salamon, M. ^{[1
]}

机构：

[1] Wroclaw Univ Sci & Technol, Fac Chem, Wybrzeze Wyspianskiego 27, PL-50370 Wroclaw, Poland

[2] Ecole Polytech, Mecan Energet, Technopole Chateau Gombert,5 Rue Enrico Fermi, F-13453 Marseille 13, France

来源：

JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY | 2023年 / 148卷 / 09期

关键词：

Phase diagram; DSC; Ytterbium(II) chloride; Lithium chloride; Sodium chloride; Thermodynamic functions; CALPHAD method; EUCL2;

D O I：

10.1007/s10973-022-11813-7

中图分类号：

O414.1 [热力学];

学科分类号：

摘要：

Differential scanning calorimetry technique was used to investigate phase equilibria in the YbCl2-MCl (M = Li, Na) binary systems. The YbCl2-LiCl system exhibits an eutectic located at YbCl2 mole fraction x = 0.415 (733 K) and a LiYb2Cl5 stoichiometric compound that is formed at 711 K and melts incongruently at 742 K. The YbCl2-NaCl system exhibits an eutectic located at YbCl2 mole fraction x = 0.559 (764 K). In both systems the formation of solid solutions in the MCl-rich side (M = Li, Na) has been found. The molar enthalpies of mixing (Delta H-MIX) in the liquid YbCl2-MCl (M = Na, K) mixtures have been measured at 1085 K with a Calvet-type high temperature microcalorimeter in the entire range of composition. A negative value of mixing enthalpy was observed for all melts. The minimum value was of approximately: - 2.5, and - 7.5 kJ mol(-1), for systems with NaCl and KCl, respectively. All the experimental results along with the available literature data were used to optimize the thermodynamic properties of the investigated systems using the CALPHAD method.

引用

页码：3515 / 3523

页数：9

共 22 条

[1]

Blasse G., 1994, Luminescent Materials

[2]

Da Silva F, 2001, Z NATURFORSCH A, V56, P653

[3] Preparation and spectroscopy of Yb2+-doped Y3Al5O12, YAlO3, and LiBaF3 [J].