Evolution mechanism of interfacial microstructure and its effect on failure in dissimilar metal welds containing ferritic heat resistant steels

被引:6
作者
Li, Xiaogang [1 ]
Nie, Junfeng [1 ]
Wang, Xin [1 ]
Li, Kejian [2 ]
Cai, Zhipeng [2 ]
Zhang, Haiquan [1 ]
机构
[1] Tsinghua Univ, Inst Nucl & New Energy Technol, Key Lab Adv Reactor Engn & Safety, Minist Educ, Beijing 100084, Peoples R China
[2] Tsinghua Univ, Dept Mech Engn, Beijing 100084, Peoples R China
来源
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T | 2023年 / 26卷
关键词
Dissimilar metal weld; Ferritic heat resistant steel; Interface structure; Microstructure evolution; Creep failure; POWER-PLANTS; BOILER MATERIALS; STAINLESS-STEEL; SHEAR-STRESS; TRANSITION; BEHAVIOR; ALLOY; PERFORMANCE; JOINTS;
D O I
10.1016/j.jmrt.2023.09.036
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This study investigated the behaviour and mechanism of interfacial microstructure evo-lution during long term high temperature exposure and the effect of interface structure on creep failure in the dissimilar metal welds (DMWs) involving ferritic heat resistant steels with nickel-based filler metal. The welding of nickel-based and ferritic materials led to the formation of interfacial martensite layer in the ferritic steel side of DMW. During long term high temperature exposure, interfacial martensite transformed to ferrite due to C diffusion and migration in the micro-region near the BCC/FCC interface between the martensite layer and the weld metal. The martensite-ferrite transformation was attributed to the large C chemical potential gradient caused by chemical composition gradient. Under creep condition, the failure of DMW was prone to occur along the weld metal/ferritic steel interface, which was related to strain concentration around the interfacial ferrite formed during service. Hence, the relationships between interface structures before and after service and interfacial failure in the DMWs were clarified.(c) 2023 The Authors. Published by Elsevier B.V.This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
引用
收藏
页码:6565 / 6580
页数:16
相关论文
共 35 条
[1]   Progress in Creep-Resistant Steels for High Efficiency Coal-Fired Power Plants [J].
Abe, Fujio .
JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2016, 138 (04)
[2]   Precipitate design for creep strengthening of 9% Cr tempered martensitic steel for ultra-supercritical power plants [J].
Abe, Fujio .
SCIENCE AND TECHNOLOGY OF ADVANCED MATERIALS, 2008, 9 (01)
[3]  
BRUN MK, 1988, ADV CERAM MATER, V3, P506
[4]   High-efficiency coal-fired power plants development and perspectives [J].
Bugge, Jorgen ;
Kjaer, Sven ;
Blum, Rudolph .
ENERGY, 2006, 31 (10-11) :1437-1445
[5]  
Christoffel R.J., 1956, Weld. J, V35, p457s
[6]  
DuPont JN, 2007, WELD J, V86, p51S
[7]   Microstructural evolution and high temperature failure of ferritic to austenitic dissimilar welds [J].
DuPont, J. N. .
INTERNATIONAL MATERIALS REVIEWS, 2012, 57 (04) :208-234
[8]   Homogenizing interfacial shear stress via thickness gradient [J].
Gao, Yang ;
Yao, Haimin .
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2019, 131 :112-124
[9]  
GITTOS MF, 1992, WELD J, V71, pS461
[10]   Measurement of geometrically necessary dislocation density with high resolution electron backscatter diffraction: Effects of detector binning and step size [J].
Jiang, J. ;
Britton, T. B. ;
Wilkinson, A. J. .
ULTRAMICROSCOPY, 2013, 125 :1-9