Effect of High-Energy Ball Milling in Toluene on the Morphology, Phase Evolution, and Contamination for Some Elemental Powders

被引:4
作者
Behera, Kishore Kumar [1 ]
Pradeep, K. G. [1 ]
Bakshi, Srinivasa Rao [1 ]
机构
[1] Indian Inst Technol Madras, Dept Met & Mat Engn, Chennai 600036, India
来源
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2024年 / 55卷 / 01期
关键词
PROCESS-CONTROL AGENTS; MECHANICAL-PROPERTIES; HYDRIDE FORMATION; RAMAN-SCATTERING; SOLID-STATE; AL-ZR; MICROSTRUCTURE; TITANIUM; TI; CARBIDE;
D O I
10.1007/s11661-023-07250-2
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This study reports the effect of milling time on the carbon content, morphology, crystallite size, and phase evolution of pure elemental Al, Fe, Ni, Cu, Cr, Mo, Si, Co, W, V, Ta, and Ti powders during high-energy ball milling (HEBM) in toluene. The XRD results show that the HEBM of Ti resulted in the formation of TiCx, which was confirmed by Raman Spectroscopy, while milling of Ta resulted in the formation of TaCx and TaHx. In comparison, there was no carbide or hydride phase formation up to 20 hours of milling for all other elemental powders. The weight percentage of carbon in the milled powder was observed to increase progressively with milling time. Ti powder showed the highest wt pct of C followed by Ta, W, Si, Al, Cr, Fe, Mo, V, Co, Ni, and Cu, respectively. The presence of carbon could be attributed to the dissociation of toluene and erosion of tungsten carbide balls and vials. The results show that carbon pickup significantly depends on the element being milled. The D50 particle size reduced appreciably after 20 hours of milling. The crystallite size for all the powders reduced progressively with milling time and was found to be in the range of 20 to 36 nm after 20 hours of milling.
引用
收藏
页码:303 / 319
页数:17
相关论文
共 82 条
  • [31] PHASE-TRANSFORMATIONS INDUCED BY MECHANICAL ALLOYING IN BINARY-SYSTEMS
    MA, E
    ATZMON, M
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 1995, 39 (04) : 249 - 267
  • [32] Formation of face-centered-cubic titanium by mechanical attrition
    Manna, I
    Chattopadhyay, PP
    Nandi, P
    Banhart, F
    Fecht, HJ
    [J]. JOURNAL OF APPLIED PHYSICS, 2003, 93 (03) : 1520 - 1524
  • [33] Rietveld refinement guidelines
    McCusker, LB
    Von Dreele, RB
    Cox, DE
    Louër, D
    Scardi, P
    [J]. JOURNAL OF APPLIED CRYSTALLOGRAPHY, 1999, 32 : 36 - 50
  • [34] Murty BS, 1998, INT MATER REV, V43, P101, DOI 10.1179/095066098790105654
  • [35] Influence of benzene on the Ni3Fe nanocrystalline compound formation by wet mechanical alloying: An investigation combining DSC, X-ray diffraction, mass and IR spectrometries
    Neamtu, B. V.
    Isnard, O.
    Chicinas, I.
    Vagner, C.
    Jumate, N.
    Plaindoux, P.
    [J]. MATERIALS CHEMISTRY AND PHYSICS, 2011, 125 (03) : 364 - 369
  • [36] AN EXPERIMENTAL INVESTIGATION OF EXTRAPOLATION METHODS IN THE DERIVATION OF ACCURATE UNIT-CELL DIMENSIONS OF CRYSTALS
    NELSON, JB
    RILEY, DP
    [J]. PROCEEDINGS OF THE PHYSICAL SOCIETY OF LONDON, 1945, 57 (321): : 160 - 177
  • [37] HYDRIDE FORMATION IN MECHANICALLY ALLOYED AL-ZR AND AL-FE-ZR
    NIU, XP
    FROYEN, L
    DELAEY, L
    PEYTOUR, C
    [J]. SCRIPTA METALLURGICA ET MATERIALIA, 1994, 30 (01): : 13 - 18
  • [38] Nanocrystalline metals prepared by low energy ball milling
    Oleszak, D
    Shingu, PH
    [J]. JOURNAL OF APPLIED PHYSICS, 1996, 79 (06) : 2975 - 2980
  • [39] Pachfule P, 2016, NAT CHEM, V8, P718, DOI [10.1038/NCHEM.2515, 10.1038/nchem.2515]
  • [40] Peterson N.L., 1982, DIFFUSION MECH GRAIN