Potential utilization of oil sludge incineration bottom ash for glass-ceramics: Crystallization kinetics, properties and toxicological evaluation

The bottom ash (OIBA) generated from the incineration of hazardous oil sludge is classified as a hazardous waste. In this work, the OIBA was applied as raw material to prepare SiO2-Al2O3-CaO system glass-ceramics by melt sintering with the addition of waste glass wool (GW). The effects of basicity (CaO/SiO2 ratio, 0.52-1.05) and sintering temperature (900-1050 degrees C) on the crystallization kinetics, properties, microstructure, leaching concentrations of heavy metals and potential toxicity of glass-ceramics were investigated. The results showed that the crystallization pattern was two-dimensional crystallization, and with the decrease of basicity, the main crystalline phase evolved from gehlenite to diopside. And the glass-ceramics with basicity of 0.88 and sintering temperature of 950 degrees C exhibited the best comprehensive properties, including density (2.72 g/cm3), water absorption (0.06%), compressive strength (452.45 MPa) and chemical corrosion resistance. In addition, the reduction of heavy metal leaching concentration indicates that produced glass-ceramics showed excellent solidification effect on heavy metals, the low toxicity of glass-ceramics leaching solution to the wheat seeds and Artemia suggests the environmental protection characteristics of OIBA-based glass-ceramics. These findings proved that the glass-ceramics produced by OIBA and GW could be a promising method to dispose hazardous waste with preparing high value-added construction materials.