Production and characterization of briquettes from sugarcane bagasse of Wonji Sugar Factory, Oromia, Ethiopia

Briquetted biomass, like sugarcane bagasse, a by-product of sugar mills, is a renewable energy source. This study aimed at the production and characterization of bagasse briquettes. The production of briquettes was carried out with different blending ratios (5, 10, and 15%) and average particle sizes (0.75, 2.775, and 4.8 mm) with various binders of cow dung, waste paper, and admixture (molasses and wastepaper). The bagasse underwent drying, size reduction, sieving, binder addition, and densification using a manual press during the briquetting process. Characterization of the physical and combustion parameters of briquettes, such as density, shatter resistance, proximate, and calorific value, followed the American Society for Testing and Materials procedures. The result shows that the maximum density of briquettes was 0.804 g/cm(3), while shatter resistance varied from 83.051 to 94.975% (4.8mm, 5% cow dung and 0.75mm, 5% admixture binders respectively). ANOVA analysis showed that the factors and their interactions had a significant influence (p value < 0.05) on the physical properties. The optimum parameters of briquettes achieved were 14.953% admixture binder, 0.776 mm particle size, 0.805 g/cm3 density, and 95.811% shatter resistance. Bagasse briquettes with a 5% cow dung binder achieved a high calorific value of 39927.05 kcal/kg. The ultimate analysis revealed a composition of 47.49% carbon (C), 5.133% hydrogen (H), 1.557% nitrogen (N), 0.374% sulfur (S), and 45.446% oxygen (O). Therefore, bagasse has a high calorific value and can be used for briquetting to replace fossil fuel and firewood in different applications. In addition, due to its availability, utilizing as fuel source has economic advantage.