High-temperature magnetic performance and corrosion resistance of hot-deformed and sintered Nd-Fe-B magnets with similar room-temperature magnetic properties

被引：4

作者：

Dai, Ge ^{[1
,2
]}

Yin, Wenzong ^{[2
,3
]}

Tang, Xu ^{[2
]}

Ju, Jinyun ^{[2
]}

Wu, Lian ^{[2
]}

Cui, Yuhang ^{[1
,2
]}

Chen, Renjie ^{[1
,2
,3
]}

Yan, Aru ^{[2
,3
]}

机构：

[1] Ningbo Univ, Sch Mat Sci & Chem Engn, Ningbo 315211, Peoples R China

[2] Chinese Acad Sci, Ningbo Inst Mat Technol & Engn, CISRI & NIMTE Joint Innovat Ctr Rare Earch Permane, Ningbo 315201, Peoples R China

[3] Univ Chinese Acad Sci, Beijing 100049, Peoples R China

来源：

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS | 2023年 / 587卷

关键词：

Hot-deformed magnet; Irreversible flux loss; Temperature coefficient of coercivity; Corrosion resistance; Grain size; Grain boundary; THERMAL-STABILITY; NDFEB MAGNETS; INTERGRANULAR ADDITION; PERMANENT-MAGNETS; COERCIVITY; MICROSTRUCTURES; SUBSTITUTION; DIFFUSION; LOSSES; TIME;

D O I：

10.1016/j.jmmm.2023.171321

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Both hot-deformed (HD) and sintered Nd-Fe-B magnet have huge prospect in the application of permanent magnet servomotor, but its magnetic performance is often influenced by increased working temperature and corrosion environment. Hereby, the high-temperature magnetic performance and corrosion resistance of HD magnets and sintered magnets with similar room-temperature magnetic properties were investigated. The melt-spun Nd-Fe-B powders of MQU-F and MQU-G have been used to prepare the HD magnets without (HDF) and with (HDG) heavy rare earth of Dy element. The sintered magnets of 45H grade (S45H) and 35UH grade (S35UH) were used as reference magnets to evaluate the high-temperature magnetic performance and corrosion resistance of HDF and HDG, respectively. The results show that both HDF and HDG have superior temperature coefficient of coercivity (beta), irreversible flux loss (hirr) and corrosion resistance to the same-grade sintered magnets. The analysis on microstructure and element composition reveals that the difference in beta and hirr between HD and sintered magnets is mainly resulted from grain size and Pr content. The nanograins in HD magnets are much smaller than the micrograins in sintered magnets. Consequently, |beta| and hirr reduces significantly with the decrease of grain size. Meanwhile, the Pr-contained sintered magnets of S45H and S35UH consist of both Pr2Fe14B and Nd2Fe14B phases. As the magneto-crystalline anisotropy of Pr2Fe14B decreases faster than that of Nd2Fe14B with the increased temperature. |beta| and hirrof the HDF and HDG are better than those of the same-grade sintered magnets. In addition, the difference in corrosion resistance is primarily caused by the grain boundary (GB) width, the total rare earth (TRE) content and Co content. The corrosion on Nd-Fe-B magnet initiates from and propa-gates along GB and the boundary of flake particles at the surface of HD and sintered magnets. The narrower GB width, lower TRE content and higher Dy content all play important role in better corrosion resistance of HD magnets.

引用

页数：10

共 33 条

[1]

[Anonymous], 2007, GB/T 13560-2017

[2] CORROSION OF RAPIDLY SOLIDIFIED NEODYMIUM-IRON-BORON (ND-FE-B) PERMANENT-MAGNETS AND PROTECTION VIA SACRIFICIAL ZINC COATINGS [J].

ATTANASIO, SA ;

LATANISION, RM .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1995, 198 (1-2) :25-34

[3]

Bala H, 1998, BRIT CORROS J, V33, P37, DOI 10.1179/000705998798114732

[4] Developments in the processing and properties of NdFeb-type permanent magnets [J].

Brown, D ;

Ma, BM ;

Chen, ZM .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2002, 248 (03) :432-440

[5] THE TEMPERATURE STABILITY OF NDFEB AND NDFEBCO MAGNETS [J].

CLEGG, AG ;

COULSON, IM ;

HILTON, G ;

WONG, HY .

IEEE TRANSACTIONS ON MAGNETICS, 1990, 26 (05) :1942-1944

[6] Effect of Dy2O3 intergranular addition on thermal stability and corrosion resistance of Nd-Fe-B magnets [J].

Cui, X. G. ;

Cui, C. Y. ;

Cheng, X. N. ;

Xu, X. J. .

INTERMETALLICS, 2014, 55 :118-122

[7] CORROSION OF NDFEB PERMANENT-MAGNETS IN HUMID ENVIRONMENTS AT TEMPERATURES UP TO 150-DEGREES-C [J].

CYGAN, DF ;

MCNALLAN, MJ .

JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1995, 139 (1-2) :131-138

[8] Estimation of Time-Dependent Polarization Losses in Sintered Nd-Fe-B Permanent Magnets [J].

Haavisto, Minna ;

Kankaanpaa, Harri ;

Paju, Martti .

IEEE TRANSACTIONS ON MAGNETICS, 2011, 47 (01) :170-174

[9] Temperature Stability and Flux Losses Over Time in Sintered Nd-Fe-B Permanent Magnets [J].

Haavisto, Minna ;

Paju, Martti .

IEEE TRANSACTIONS ON MAGNETICS, 2009, 45 (12) :5277-5280

[10] MAGNETIZATION AND MAGNETIC-ANISOTROPY OF R2FE14B MEASURED ON SINGLE-CRYSTALS [J].

HIROSAWA, S ;

MATSUURA, Y ;

YAMAMOTO, H ;

FUJIMURA, S ;

SAGAWA, M ;

YAMAUCHI, H .

JOURNAL OF APPLIED PHYSICS, 1986, 59 (03) :873-879

← 1 2 3 4 →