Preparation of Molybdenum-Tungsten Alloy Powders via Magnesium and Calcium Vapor Reduction of Oxide Compounds

被引：0
作者：
Kolosov, V. N. [1 ]
Miroshnichenko, M. N. [1 ]
Prokhorova, T. Yu. [1 ]
机构：
[1] Russian Acad Sci, Tananaev Inst Chem, Fed Res Ctr, Kola Sci Ctr, Apatity 184209, Murmansk Oblast, Russia
来源：
INORGANIC MATERIALS | 2023年 / 59卷 / 09期
关键词：
powder; alloy; reduction; specific surface area; porosity; SELECTIVE HYDRODEOXYGENATION; GUAIACOL; BEHAVIOR;
D O I：
10.1134/S0020168523090078
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We report the preparation of molybdenum-tungsten alloy powders via magnesium and calcium vapor reduction of the Mo0.3W0.7O3, Mg\Mo0.7W0.3O4, and Ca\Mo0.7W0.3O4 compounds in the temperature range 750-880 degrees C at residual pressures in the reactor from 5 to 15 kPa. The specific surface area of the Mo-W alloy powders prepared by reducing Mo0.3W0.7O3 slightly exceeds that of the mixture of metal powders obtained by reducing a mixture of WO3 and MoO3 under similar conditions. The specific surface area of the Mo-W alloy powders prepared via magnesium vapor reduction of the Ca\Mo0.7W0.3O4 and Mg\Mo0.7W0.3O4 compounds exceeds that in the case of calcium vapor reduction. We have obtained molybdenum-tungsten alloy powders having lattice parameters of 0.3153 +/- 0.0001 and 0.3160 +/- 0.0001 nm and ranging in specific surface area from 9 to 22 m(2)/g. The average crystallite size of the alloys, evaluated using the Scherrer formula, lies in the range 12-35 nm. The powders have a mesoporous structure.
引用
收藏
页码：940 / 948
页数：9
相关论文
共 26 条
  • [1] Studies on the synthesis of a Mo-30 wt% W alloy by non-conventional approaches
    Chakraborty, S. P.
    Banerjee, S.
    Sanyal, Gopal
    Bhave, V. S.
    Paul, Bhaskar
    Sharma, I. G.
    Suri, A. K.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 501 (02) : 211 - 217
  • [2] Sol-gel synthesis and characterization of tungsten-molybdenum solid solution nanoparticles
    Chen, Qiuyu
    Liang, Shuhua
    Li, Bingxue
    Chen, Zheng
    Song, Xiaoyan
    Zhuo, Longchao
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2021, 100
  • [3] Preparation and characterization of WMo solid solution nanopowders with a wide composition range
    Chen, Qiuyu
    Liang, Shuhua
    Zhang, Junlu
    Zhang, Xiaochuan
    Wang, Chan
    Song, Xiaoyan
    Zhuo, Longchao
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 823
  • [4] Cullity B.D., 2001, ELEMENTS XRAY DIFFRA
  • [5] Comparative study of NiW, NiMo and MoW prepared by mechanical alloying
    Gonzalez, G.
    Sagarzazu, A.
    Villalba, R.
    Ochoa, J.
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 434 (SPEC. ISS.) : 525 - 529
  • [6] Ultrafast synthesis of nanocrystalline molybdenum powder by thermal plasma and its sintering behavior
    Hu, Peng
    Chen, Tingyi
    Li, Xiaojing
    Gao, Junyan
    Chen, Shuqun
    Zhou, Wenyuan
    Wang, Jinshu
    [J]. INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2019, 83
  • [7] Calcium Vapor Reduction of Group V and VI Metal Oxide Compounds
    Kolosov, V. N.
    Orlov, V. M.
    Miroshnichenko, M. N.
    [J]. INORGANIC MATERIALS, 2020, 56 (01) : 35 - 41
  • [8] Electronically Mediated Reactions in Metal Thermal Reduction of Molybdenum and Tungsten Oxide Compounds
    Kolosov, V. N.
    Orlov, V. M.
    [J]. DOKLADY PHYSICAL CHEMISTRY, 2019, 484 (2) : 28 - 31
  • [9] Lassner E., 1999, Tungsten, DOI [10.1007/978-1-4615-4907-9, DOI 10.1007/978-1-4615-4907-9]
  • [10] Bimetallic molybdenum-tungsten carbide/reduced graphene oxide hybrid promoted Pt catalyst with enhanced electrocatalytic activity and stability for direct methanol fuel cells
    Li, Suwen
    Zhang, Yu
    Han, Yuanxia
    Lv, Fangfei
    Liu, Baocang
    Huo, Lili
    [J]. APPLIED SURFACE SCIENCE, 2022, 600
123