Optical Properties Investigation of Upconverting K2Gd(PO4)(WO4):20%Yb3+,Tm3+ Phosphors

Nowadays, scientists are interested in inorganic luminescence materials that can be excited with UV or NIR radiation and emit in the visible range. Such inorganic materials can be successfully used as luminescent or anti-counterfeiting pigments. In this work, we report the synthesis and optical properties investigation of solely Tm3+ doped and Yb3+/Tm3+ co-doped K2Gd(PO4)(WO4) phosphors. The single-phase samples were prepared using a solid-state reaction method. The Tm3+ concentration was changed from 0.5% to 5%. Downshifting and upconversion emission studies were performed under 360 nm and 980 nm excitation, respectively. Yb3+ ions were used as sensitizers in the K2Gd(PO4)(WO4) phosphors to transfer the captured energy to Tm3+ ions. It turned out that under UV excitation, phosphors emitted in the blue spectral area regardless of the presence or absence of Yb3+. However, a very strong deep-red (similar to 800 nm) emission was observed when Yb3+ and Tm3+-containing samples were excited with a 980 nm wavelength laser. It is interesting that the highest upconversion emission in the UV/Visible range was achieved for 20% Yb3+, 0.5% Tm3+ doped sample, whereas the sample co-doped with 20% Yb3+, 2% Tm3+ showed the most intensive UC emission band in the NIR range. The materials were characterized using powder X-ray diffraction and scanning electron microscopy. Optical properties were studied using steady-state and kinetic downshifting and upconversion photoluminescence spectroscopy.