Corrosion cracking behavior of reinforced concrete under freeze-thaw cycles

被引：31
|
作者：
Liu, Xiguang [1 ,2 ]
Yan, Ziwei [2 ]
Wang, Dongjing [3 ]
Zhao, Rong [2 ,4 ]
Niu, Ditao [1 ,2 ]
Wang, Yan [5 ]
机构：
[1] Xian Univ Architecture & Technol, State Key Lab Green Bldg Western China, 13 Yanta Rd, Xian 710055, Peoples R China
[2] Xian Univ Architecture & Technol, Coll Civil Engn, 13 Yanta Rd, Xian 710055, Peoples R China
[3] China JiKan Res Inst Engn Invest & Design Co Ltd, 51 Xianning Rd, Xian 710043, Peoples R China
[4] Beijing Glory PKPM Technol Co Ltd, 30 North Third Ring Rd East, Beijing 100013, Peoples R China
[5] Xian Univ Architecture & Technol, Coll Mat & Engn, 13 Yanta Rd, Xian 710055, Peoples R China
来源：
JOURNAL OF BUILDING ENGINEERING | 2023年 / 64卷
基金：
中国国家自然科学基金;
关键词：
Reinforced concrete; Freeze-thaw cycles; Corrosion cracking; Damaged layer thickness; TIME; SURFACE;
D O I：
10.1016/j.jobe.2022.105610
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
This paper presents an experimental and theoretical study on the corrosion cracking behavior of reinforced concrete under freeze-thaw cycles. Accelerated corrosion tests were carried out on reinforced concrete specimens subjected to freeze-thaw cycles. The test results of Digital Image Correlation (DIC) showed that the cracking positions on the concrete surface were randomly distributed. The critical corrosion ratio of reinforcing bars decreased with increasing freeze-thaw cycles. The reinforcing bar critical corrosion ratio at cover cracking under freeze-thaw environ-ment was established with the thick-walled double cylinder theory, and was in acceptable with experimental results.
引用
收藏
页数：14
相关论文
共 50 条
  • [31] Experimental study on seismic behavior of recycled concrete brick walls under freeze-thaw cycles
    Zheng, Shansuo
    Shang, Xiaoyu
    Zhang, Kui
    Liang, Xianfeng
    Ma, Delong
    Jianzhu Jiegou Xuebao/Journal of Building Structures, 2015, 36 (03): : 64 - 70
  • [32] Damage Mechanism and Modeling of Concrete in Freeze-Thaw Cycles: A Review
    Guo, Jinjun
    Sun, Wenqi
    Xu, Yaoqun
    Lin, Weiqi
    Jing, Weidong
    BUILDINGS, 2022, 12 (09)
  • [33] Deterioration of concrete under the coupling effects of freeze-thaw cycles and other actions: A review
    Wang, Ruijun
    Zhang, Qingjun
    Li, Yang
    CONSTRUCTION AND BUILDING MATERIALS, 2022, 319
  • [34] Study on the bonding performance between basalt textile and concrete under freeze-thaw cycles
    Cai, Shixing
    Lin, Jianhong
    Fan, Kaifang
    Chen, Yuanyi
    Wang, Zeping
    ENGINEERING FAILURE ANALYSIS, 2023, 146
  • [35] Compression behavior of CFRP-confined recycled aggregate concrete under combined effects of sulfate corrosion and freeze-thaw cycles
    Peng, Sheng
    Min, Tian-run
    Peng, Shuang
    Xie, Xian-qi
    Yao, Ying-kang
    Jia, Yong-sheng
    CONSTRUCTION AND BUILDING MATERIALS, 2025, 473
  • [36] Study on the strength size effect of wastewater concrete under freeze-thaw cycles
    Guan, Junfeng
    Liu, Li
    Yao, Xianhua
    Meng, Jiangfeng
    Han, Linyan
    CONSTRUCTION AND BUILDING MATERIALS, 2024, 438
  • [37] Behavior of concrete-filled circular steel tubular stub columns exposed to corrosion and freeze-thaw cycles
    Lyu, Xuetao
    Zhang, Tong
    Wang, Weiwei
    Zhang, Liqiang
    Xue, Guofeng
    STRUCTURES, 2023, 55 : 2266 - 2279
  • [38] Influence of Freeze-thaw Cycles on Multiaxial Strength of Concrete
    Qin, Likun
    Gao, Lingxia
    Song, Hongwei
    PROGRESS IN INDUSTRIAL AND CIVIL ENGINEERING II, PTS 1-4, 2013, 405-408 : 2715 - 2718
  • [39] Chloride penetration in freeze-thaw induced cracking concrete: A numerical study
    Li, Lin-jie
    Liu, Qing-feng
    Tang, Luping
    Hu, Zhe
    Wen, Yong
    Zhang, Peng
    CONSTRUCTION AND BUILDING MATERIALS, 2021, 302
  • [40] Dynamic Behavior of Rubber Fiber-Reinforced Expansive Soil under Repeated Freeze-Thaw Cycles
    Sun, Zhenxing
    Wang, Rongchang
    Yang, Zhongnian
    Lv, Jianhang
    Shi, Wei
    Ling, Xianzhang
    POLYMERS, 2024, 16 (19)
12345