Electrochemical responses of carbon steel in ordinary Portland cement blended with calcium sulfoaluminate cement

被引：4

作者：

Geng, Zhi ^{[1
]}

Liu, Yongqi ^{[1
]}

Shi, Jinjie ^{[1
]}

机构：

[1] Southeast Univ, Sch Mat Sci & Engn, Jiangsu Key Lab Construct Mat, Nanjing 211189, Peoples R China

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2023年 / 400卷

关键词：

Carbon steel; Sulfoaluminate cement; Passivation; Chloride-induced corrosion; Pore solution; PORE SOLUTION CHEMISTRY; REINFORCING STEEL; CORROSION BEHAVIOR; IMPEDANCE SPECTROSCOPY; PITTING CORROSION; CONCRETE; CHLORIDE; PASSIVATION; FILM; TEMPERATURE;

D O I：

10.1016/j.conbuildmat.2023.132788

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This work investigated the passivation and chloride-induced corrosion of carbon steel exposed to an extract solution (PCSA) of ordinary Portland cement (OPC) blended with calcium sulfoaluminate (CSA) cement. As evaluated by EIS and XPS measurements, carbon steel gained inferior passivity by forming a thinner and less protective passive film in PCSA solution compared with that in the pure OPC solution. However, after chloride attack, comparable corrosion resistance was confirmed for steel exposed to both solutions. Furthermore, enhanced pitting corrosion resistance was identified for steel after 30 d of immersion in PCSA solution, which was mainly attributed to the formation of an Al-rich layer on the steel surface as well as the reduced chloride concentration in solution by the unreacted aluminum phase.

引用

页数：11

共 58 条

[1] Environmental factors affecting the corrosion behaviour of reinforcing steel. V. Role of chloride and sulphate ions in the corrosion of reinforcing steel in saturated Ca(OH)2 solutions [J].

Abd El Haleem, S. M. ;

Abd El Wanees, S. ;

Bahgat, A. .

CORROSION SCIENCE, 2013, 75 :1-15

[2] Environmental factors affecting the corrosion behaviour of reinforcing steel: I. The early stage of passive film formation in Ca(OH)2 solutions [J].

Abd El Haleem, S. M. ;

Abd El Aal, E. E. ;

Abd El Wanees, S. ;

Diab, A. .

CORROSION SCIENCE, 2010, 52 (12) :3875-3882

[3]

Alhozaimy A, 2014, ACI MATER J, V111, P411

[4] Pore solution composition of calcium sulfoaluminate cement [J].

Andac, M ;

Glasser, FP .

ADVANCES IN CEMENT RESEARCH, 1999, 11 (01) :23-26

[5] Kinetics of carbon steel dissolution in ammonium chloride solution containing sodium thiosulfate [J].

Baranwal, Prince Kumar ;

Rajaraman, Prasanna Venkatesh .

INTERNATIONAL JOURNAL OF CHEMICAL KINETICS, 2019, 51 (07) :497-510

[6] Estimating Critical Corrosion for Initiation of Longitudinal Cracks in RC Structures Considering Phases and Composition of Corrosion Products [J].

Behera, Prasanna Kumar ;

Moon, Abhijeet Prem Kumar ;

Mondal, Kallol ;

Misra, Sudhir .

JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2016, 28 (12)

[7] Behavior of blends of CSA and Portland cements in high chloride environment [J].

Bertola, Federica ;

Gastaldi, Daniela ;

Irico, Sara ;

Paul, Geo ;

Canonico, Fulvio .

CONSTRUCTION AND BUILDING MATERIALS, 2020, 262

[8] Study on the adsorption of OH- and CaOH+ on Fe (100) surface and their effect on passivation of steel bar: Experiments and DFT modelling [J].

Chen, Zheng ;

Nong, Yumei ;

Chen, Ye ;

Chen, Jianhua ;

Yu, Bo .

CORROSION SCIENCE, 2020, 174

[9] Pathways towards sustainable concrete [J].

Coffetti, D. ;

Crotti, E. ;

Gazzaniga, G. ;

Carrara, M. ;

Pastore, T. ;

Coppola, L. .

CEMENT AND CONCRETE RESEARCH, 2022, 154

[10] Calcium sulfoaluminate cement blended with OPC: A potential binder to encapsulate low-level radioactive slurries of complex chemistry [J].

Coumes, Celine Cau Dit ;

Courtois, Simone ;

Peysson, Sandrine ;

Ambroise, Jean ;

Pera, Jean .

CEMENT AND CONCRETE RESEARCH, 2009, 39 (09) :740-747

← 1 2 3 4 5 6 →