Hybrid Zinc Coatings with Chitosan/Alginate Encapsulated CuO-Nanoparticles for Anticorrosion and Antifouling Protection of Mild Steel

The construction of anticorrosion coatings containing antifouling agents is an effective way to ensure the long-term durability of marine steel infrastructures. In this work, an innovative hybrid coating was prepared by introducing biocide CuO nanoparticles in ordinary zinc coating to improve its protective ability for steel in aggressive salt water environments. The CuO nanoparticles were embedded inside the matrix of chitosan/alginate complexes to prevent spontaneous copper leaching during corrosive attacks. Two procedures were applied for the electrodeposition of hybrid/composite zinc-based coatings on low-carbon steel substrates (DC current): first-the co-electrodeposition of encapsulated CuO nanoparticles with zinc on a cathode (steel) electrode from a sulfate electrolyte with a relatively low pH value of about 4.5-5.0 and second-the encapsulated CuO nanoparticles were electrodeposited from aqueous solution as an intermediate layer between two zinc deposits. The particles size and stability of suspensions were evaluated using dynamic light scattering. Both hybrid coatings were compared in terms of surface morphology and hydrophilicity (SEM and AFM analysis, contact angle measurement) and corrosion resistance (potentiodynamic polarization curves, polarization resistance). The protective characteristics of the coatings were compared in a 3.5% NaCl solution and artificial sea water. The hybrid coating showed 2-4 times higher polarization resistance than the bare zinc coating during a 30 day immersion in artificial sea water, indicating that this coating has the necessary characteristics to be used in a marine environment.