Composite of Poly(Vinyl Chloride) Plastisol and Wood Flour as a Potential Coating Material

This paper presents the results of a study of the properties of a new composite material made from poly(vinyl chloride) plastisol (PVC) and conifer-derived wood flour. The material can be used for thermal insulation, floor coverings with high resistance to mechanical trauma, and protective coatings. The plastisol was made from emulsion poly(vinyl chloride), the plasticiser was bis(2-ethylhexyl) adipate, and the stabiliser was octyltin mercapeptide. Two types of flour were used: fine-grained and coarse-grained. Its properties, such as bulk density, oil number, and plasticiser number, were determined. The polymer-wood composite contained 20 or 30 wt.% wood flour in PVC. Plastisol was obtained by repeated mixing, mashing, and venting under vacuum. The produced composite material was gelated at temperatures of 130, 150, and 170 degrees C. The gelation process of the composites was studied in a Brabender apparatus. Samples in the form of polymer films were used to study density, hardness, thermal stability, and mechanical and thermomechanical properties. The structure of the composites was observed by scanning electron microscopy (SEM). A summary of all test results showed that composite films made from PVC plastisol with 20 wt.% of fine wood flour gelled at 150 degrees C had the most favourable physical, mechanical, and thermal properties.