MICROSTRUCTURE AND PROPERTIES EVALUATION OF DUCTILE CAST IRON SUBJECTED TO HOT PLASTIC DEFORMATION AND AMBIENT TEMPERATURE COMPRESSION

被引：3

作者：

Chaus, A. S. ^{[1
]}

Caplovic, E. ^{[1
]}

Pokrovskii, A. I. ^{[2
]}

Sobota, R. ^{[1
]}

机构：

[1] Slovak Univ Technol, Fac Mat Sci & Technol, J Bottu 25, Trnava 91724, Slovakia

[2] Natl Acad Sci Belarus, Tech Inst, 10 Kuprevicha Str, Minsk 220141, BELARUS

来源：

ARCHIVES OF METALLURGY AND MATERIALS | 2023年 / 68卷 / 02期

关键词：

Ductile iron; Plastic deformation; Microstructure; Properties; Fracture surfaces; SPHEROIDAL GRAPHITE; SPECIAL FEATURES; MORPHOLOGY; BEHAVIOR; CRYSTALLIZATION; NUCLEATION; NUCLEI;

D O I：

10.24425/amm.2023.142445

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The as-cast microstructure of ductile cast iron (DI) was investigated using light microscopy (LM) and SEM techniques. Further the influence of hot plastic extrusion at 1000(degrees)C with plastic strain in the range of 20-60-80% on the transformation of the as-cast microstructure and on the mechanical properties was studied. Besides this, the microstructure of DI subjected to hot extrusion after the fracture of the corresponding samples induced by compression tests was thoroughly investigated. It was found that compression had a dramatic influence on a shear deformation and hence shear fracture of the compressed samples. It was shown that the shear fracture of the hot deformed ductile iron is accompanied by the occurrence of a narrow zone of severe plastic deformation. The fracture surfaces of the extruded samples subjected to the tensile tests and the compression tests were examined.

引用

页码：639 / 648

页数：10

共 50 条

[1] Effect of room-temperature compression on microstructure of ductile cast iron subjected to hot plastic deformation
Chaus, A. S.
PHYSICS OF METALS AND METALLOGRAPHY, 2014, 115 (07) : 672 - 681
[2] Hot compression deformation and microstructure evolution of high chromium cast iron based on canning compression
Li, Yanwei
Wang, Xiaogang
Yuan, Guofeng
Han, Peisheng
Zhu, Xiaoyu
JOURNAL OF MATERIALS SCIENCE, 2021, 56 (30) : 17296 - 17305
[3] A Study of Effect of Vanadium on Microstructure and Mechanical Properties of As-Cast and Austempered Ductile Iron
Bakhshinezhad, H.
Honarbakhshraouf, A.
Abdollah-Pour, H.
PHYSICS OF METALS AND METALLOGRAPHY, 2019, 120 (05) : 441 - 446
[4] Effect of austempering temperature on microstructure and mechanical properties of ductile cast iron modified by niobium
Sckudlarek, Wilson
Krmasha, Manar N.
Al-Rubaie, Kassim S.
Preti, Orlando
Milan, Julio C. G.
da Costa, Cesar E.
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 12 : 2414 - 2425
[5] Hot Plastic Deformation of High-Strength Cast Iron
N. P. Lyakishev
G. V. Shcherbedinskii
Metal Science and Heat Treatment, 2001, 43 : 421 - 422
[6] Hot plastic deformation of high-strength cast iron
Lyakishev, NP
Shcherbedinskii, GV
METAL SCIENCE AND HEAT TREATMENT, 2001, 43 (11-12) : 421 - 422
[7] On the Morphology Variation of Graphite in Ductile Cast Iron through Severe Plastic Deformation
S. K. Kaboli-Mallak
N. Kheirkhahan
E. Edalati
Y. Kelidari
A. R. Kiani-Rashid
Physics of Metals and Metallography, 2023, 124 : 1813 - 1825
[8] On the Morphology Variation of Graphite in Ductile Cast Iron through Severe Plastic Deformation
Kaboli-Mallak, S. K.
Kheirkhahan, N.
Edalati, E.
Kelidari, Y.
Kiani-Rashid, A. R.
PHYSICS OF METALS AND METALLOGRAPHY, 2023, 124 (14) : 1813 - 1825
[9] Process modeling, microstructure prediction and mechanical properties of sand cast ductile iron castings
Ceschini, L.
Minak, G.
Morri, Al.
Morri, An.
Tomesani, L.
Radovic, N.
Salsi, E.
Squatrito, R.
METALLURGIA ITALIANA, 2013, (01): : 2 - 11
[10] A Study of Effect of Vanadium on Microstructure and Mechanical Properties of As-Cast and Austempered Ductile Iron
H. Bakhshinezhad
A. Honarbakhshraouf
H. Abdollah-Pour
Physics of Metals and Metallography, 2019, 120 : 441 - 446

← 1 2 3 4 5 →