Preparation and Properties of Flame Retardant and Antistatic Foamed Wood-Plastic Composite with APP/ZB System

With the aggravation of fire and smoke pollution, it is urgent to develop green, lower-cost and high-performance Foamed Wood-Plastic Composite (FWPC) to meet the standards of antistatic and flame retardant in practical application. Therefore, the flame retardant and antistatic FWPCs were prepared by compression molding in this study. High-density polyethylene (PE-HD) and Salix wood flour were used as main raw materials, and azodicarbonamide (AC) was used as foaming agent; Nano-carbon black (Nano-CB) was used as antistatic filler, and ammonium polyphosphate (APP) and zinc borate (ZB) were used as flame retardants. The static bending strength and elastic modulus of FWPC-20 were up to 30.01 MPa and 2636 MPa, respectively, which can meet the commercial application of wood-plastic decorative board. The logarithm of surface resistivity and volume resistivity of FWPC-20 was kept at eight, indicating that it has antistatic effect. The residual carbon rate of FWPC-20 increased to 38.58% at 800 degrees C, indicating that FWPC had high thermal stability. The minimum heat release rate of FWPC-20 was 226.75 kw/m(2), and the average heat release rate was 110.53 kw/m(2). The total heat release was 66.96 MJ/m(2), and the Limit Oxygen Index was 27.3%, which indicated that FWPC-20 had flame retardant and smoke suppression effects. This study provides a low-cost and simple method for the design of flame retardant, antistatic and high-performance FWPC, and has broad application prospects in the fields of packaging and construction.