Perovskite SrCo0.5Fe0.25Cu0.2Nb0.05O3-d cathode for intermediate-temperature solid oxide fuel cells: Improved working stability and CO2 tolerance

Commercial solid oxide fuel cells (SOFCs) primarily operate in the intermediate temperature range (600 degrees C-800 degrees C); hence, developing cathode materials with good stability and excellent catalytic activity in this temperature range is necessary. Herein, we are reporting the performance of SrCo0.5Fe0.5O3_& delta; (SCF) and SrCo0.5Fe0.25Cu0.2Nb0.05O3_& delta; (SCFCN) perovskite oxide as cathode materials for solid oxide fuel cells (SOFCs). The SCFCN sample maintains a cubic structure under a CO2 atmosphere. The polarization resistance of the SCFCN cathode on La0.9Sr0.1Ga0.83Mg0.17O3_& delta; (LSGM) reaches 0.067 & omega;cm2 at 700 degrees C. The charge transfer and oxygen reduction reactions of the SCFCN cathode on the LSGM electrolyte are the main rate-limiting steps at 600 degrees C-700 degrees C. The SCFCN cathode maintains good electrochemical stability during a 200-h test with a configuration of SCFCN/LSGM/SCFCN symmetrical cell. Compared with SCF, the doping of Cu and Nb effectively reduces the Rp attenuation of SCFCN from 0.00012 to 0.00005 & omega;cm2/h. The output power density of the fuel cell with SCFCN as the cathode on LSGM reaches 1124 mWcm_ 2 at 800 degrees C. This indicates that SCFCN can be a potential material for fabricating cathode for intermediate-temperature SOFCs (IT-SOFCs).