Long-term behavior of prestressed concrete industrial buildings in chloride-based industrial environments

被引:7
作者
Wang, Yuwei [1 ]
Pan, Zuanfeng [1 ]
Zhao, Chengye [2 ]
Zeng, Bin [3 ]
机构
[1] Tongji Univ, Coll Civil Engn, Shanghai 200092, Peoples R China
[2] Powerchina Huadong Engn Corp Ltd, Hangzhou 311122, Peoples R China
[3] Bldg & Construct MCC Grp, Cent Res Inst, Beijing 100088, Peoples R China
来源
JOURNAL OF BUILDING ENGINEERING | 2023年 / 76卷
基金
中国国家自然科学基金;
关键词
Corrosion; Deterioration; Industrial environments; Chloride; Structural reliability; Stochastic finite element analysis; INDUCED CORROSION; ACID RESISTANCE; FLY-ASH; MODEL; DETERIORATION; RELIABILITY; CRACKING; DAMAGE;
D O I
10.1016/j.jobe.2023.107344
中图分类号
TU [建筑科学];
学科分类号
0813 ;
摘要
Combined with the main corrosive mediums existing in chloride-based industrial environments, the corrosion mechanisms of concrete and prestressing tendons are expounded, and the strength degradation law of concrete characterized by "acidification depth" with pH value and the equivalent constitutive model of prestressing wires considering stress corrosion are proposed. Taking the prestressed concrete industrial bent frame in the hydrochloric acid mist corrosion environment as a research object, the failure modes of the structural system are determined based on the elastic analysis method, and the stochastic finite element simulation is used to analyze the load effect and resistance stochastic process of the whole structure and key components. The deterioration process of load resistance and serviceability of the structure in the actual industrial environment are explored. Based on the reliability theory, the long-term behaviors of the structure under the combined action of environmental corrosion and load are studied, and the time variant failure probabilities of the main components are calculated. The results indicate that the expected service life obtained by taking the ultimate limit state of bearing capacity as the failure criterion is more accurate for actual industrial buildings, and the concentration of environmental aggressive agents exerts a significant influence on the durability and safety of key components. When the concentration of hydrochloric acid mist is 30 mg/m3, the expected life of the RC bent columns aligns well with the design service life of 50 years, while the expected life of PC crane beams is only approximately 21 years, which is much lower than the design service life, PC crane beams are more sensitive to the various of concentration of the aggressive agents than reinforced concrete columns.
引用
收藏
页数:20
相关论文
共 47 条
  • [1] American Concrete Institute, 2008, ACI2012R08
  • [2] Study on the bearing capacity and chloride ion resistance of RC structures under multi-factor corrosive environment and continuous load
    Chen, Dingshi
    Sun, Guorui
    Hu, Dalin
    Shi, Jun
    [J]. JOURNAL OF BUILDING ENGINEERING, 2021, 44
  • [3] Chen Q., 2008, THESIS SHANGHAI JIAO
  • [4] Spatial time-dependent reliability analysis of corroding pretensioned prestressed concrete bridge girders
    Darmawan, M. Sigit
    Stewart, Mark G.
    [J]. STRUCTURAL SAFETY, 2007, 29 (01) : 16 - 31
  • [5] Gu H., 2018, THESIS XIAN U ARCHIT
  • [6] Reliability analysis of corrosion initiation in reinforced concrete structures subjected to chlorides in presence of epistemic uncertainties
    Hamidane, H'mida
    Chateauneuf, Alaa
    Messabhia, Ali
    Ababneh, Ayman
    [J]. STRUCTURAL SAFETY, 2020, 86
  • [7] Effect of crack width on chloride diffusion coefficients of concrete by steady-state migration tests
    Jang, Seung Yup
    Kim, Bo Sung
    Oh, Byung Hwan
    [J]. CEMENT AND CONCRETE RESEARCH, 2011, 41 (01) : 9 - 19
  • [8] Equivalent material model of corroded prestressing steel strand
    Jeon, Chi-Ho
    Lee, Jae-Bin
    Lon, Sokanya
    Shim, Chang-Su
    [J]. JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2019, 8 (02): : 2450 - 2460
  • [9] A model for predicting carbonation of high-volume fly ash concrete
    Jiang, LH
    Lin, BY
    Cai, YB
    [J]. CEMENT AND CONCRETE RESEARCH, 2000, 30 (05) : 699 - 702
  • [10] Main considerations for the determination and evaluation of the acid resistance of cementitious materials
    Koenig, Andreas
    Dehn, Frank
    [J]. MATERIALS AND STRUCTURES, 2016, 49 (05) : 1693 - 1703