Graphene's effect and mechanism on the properties of alkali-activated slag coating

被引:2
|
作者
Wang, Siming [1 ]
Luo, Xiang [2 ]
Hua, Sudong [1 ]
Zhang, Yanan [1 ]
Chen, Tingzhu [3 ]
机构
[1] Nanjing Tech Univ, Coll Mat Sci & Engn, Nanjing 211816, Peoples R China
[2] Sinoma Suzhou Construct Co Ltd, Suzhou 215000, Jiangsu, Peoples R China
[3] Nanjing Jiangbei New Area Publ Util Holding Grp Co, Nanjing 210061, Peoples R China
关键词
geopolymer; alkali-activated slag; coating; cracking; bond strength; GEOPOLYMERS; STRENGTH; BINDERS; OXIDE;
D O I
10.1088/2053-1591/acdc85
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Using alkali-activated slag to prepare coatings is an alternative solution for concrete repair and protection. However, shrinkage cracking limits the application of alkali-activated slag, which also increases the risk of coating peeling. Graphene dispersions (content of 0.2%, 0.4%, 0.6% and 0.8%) were added to the alkali-activated slag coatings. The drying time, apparent circumstance (thicknesses of 1 mm, 2 mm, 3 mm and 5 mm) and the tensile bond strength with 1 mm thickness coating were determined. The mechanism of action was analyzed in terms of both product and interfacial properties. The experimental results showed that the graphene dispersion would shorten the drying time of the coatings. The drying time was reduced by 57.1% (from 116 min to 52 min). Moreover, the graphene dispersion improves the cracking of the coating. The larger the coating thickness is, the better it improves the cracking effect. The surface cracking of the coating with 5 mm thickness was reduced by 60.7% (from 1.6751% to 0.6583%). Graphene can significantly improve the bond strength of the coating. When the graphene content is 0.8%, the bonding strength with a thickness of 1 mm is 0.502 MPa at 7 days and 1.577 MPa at 28 days. The bond strength increased by 280.3% and 175.2%, respectively, XRD, FTIR and SEM analysis showed that the increase in bond strength was caused by two factors. (1) Graphene can promote the generation of zeolite phase in alkali-activated slag. This is conducive to enhancing the interlayer adhesion of the coating itself. (2) Graphene is beneficial to reduce the pores in the transition zone between the coating and the substrate and enhance the contact area between the coating and the substrate and makes the transition zone denser.
引用
收藏
页数:13
相关论文
共 50 条
  • [1] Effect of Graphene Oxide on Properties of Alkali-Activated Slag
    Dong, Quanwen
    Wan, Lihua
    Luan, Congqi
    Wang, Jinbang
    Du, Peng
    MATERIALS, 2021, 14 (20)
  • [2] Effect of Graphene Oxide on the Rheological Properties of Alkali-Activated Slag Paste
    Yang C.
    Huang N.
    Xie H.
    Zhu X.
    Yu L.
    2018, Tongji University (21): : 855 - 863
  • [3] Effect of super plasticizer on properties of alkali-activated slag
    Chen, K. (kechen@cqu.edu.cn), 1600, China National Publications Import and Export (Group) Corporation (34):
  • [4] Effect of admixtures on properties of alkali-activated slag concrete
    Bakharev, T
    Sanjayan, JG
    Cheng, YB
    CEMENT AND CONCRETE RESEARCH, 2000, 30 (09) : 1367 - 1374
  • [5] EFFECT OF CARBONATION ON PROPERTIES OF ALKALI-ACTIVATED SLAG BINDERS
    He, Juan
    Wu, Yonghua
    Yang, Changhui
    Gao, Qie
    Pu, Xiaolin
    REVISTA ROMANA DE MATERIALE-ROMANIAN JOURNAL OF MATERIALS, 2018, 48 (03): : 330 - 337
  • [6] Properties of alkali-activated slag cements
    Rakhimova, Nailya
    Rakhimov, Ravil
    ZKG INTERNATIONAL, 2012, 65 (11): : 32 - +
  • [7] Investigation of shrinkage mechanism of alkali-activated slag
    Wei, Yongfeng
    Dou, Hui
    He, Tingting
    Song, Kunkun
    Zhang, Qiangqiang
    CASE STUDIES IN CONSTRUCTION MATERIALS, 2024, 21
  • [8] Effect of magnesia on properties and microstructure of alkali-activated slag cement
    Fang, Yong-hao
    Liu, Jun-feng
    Chen, Yi-qun
    WATER SCIENCE AND ENGINEERING, 2011, 4 (04) : 463 - 469
  • [9] Effect of Polypropylene Fiber on Properties of Alkali-Activated Slag Mortar
    Xu, Yangchen
    Chen, Haiming
    Wang, Pengju
    ADVANCES IN CIVIL ENGINEERING, 2020, 2020