Effects of Micro-arc Oxidation Process Parameters on Micro-structure and Properties of Al2O3 Coatings Prepared on Sintered 2024 Aluminum Alloy

被引：3

作者：

Yan, Huanyuan ^{[1
]}

Liu, Wensheng ^{[1
]}

Ma, Yunzhu ^{[1
]}

Wang, Tao ^{[1
]}

Wu, Lei ^{[1
]}

Yang, Lun ^{[1
]}

Tang, Siwei ^{[1
]}

机构：

[1] Cent South Univ, Natl Key Lab Sci & Technol High Strength Struct Ma, Changsha 410083, Peoples R China

来源：

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2024年 / 33卷 / 04期

关键词：

current density; microstructure; micro-arc oxidation; oxidation time; powder metallurgy aluminum alloy; process parameters; PLASMA ELECTROLYTIC OXIDATION; CORROSION-RESISTANCE; CERAMIC COATINGS; CURRENT-DENSITY; AL; PEO;

D O I：

10.1007/s11665-023-08093-z

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, Al2O3 ceramic coatings were prepared the surface of powder metallurgy (PM) 2024 aluminum alloy via the micro-arc oxidation (MAO) technique. The effects of the current density and the oxidation treatment time on the microstructure and properties of the MAO coatings were investigated. The results reveal that the oxide film mainly comprises the gamma-Al2O3 phase, the amorphous Al2O3 phase, and a small amount of the mullite phase. There are traces of W in the coatings, which exist in the form of W, WO3, and W18O49. With increasing current density, the thickness and surface roughness of the MAO coatings prepared on the PM 2024 alloy increase, while their surface hardness first increases and then decreases. The increase in the current density promotes the transformation of the amorphous Al2O3 phase into the gamma-Al2O3 phase. The maximum hardness value of 1270 HV is obtained at a current density of 20 A dm(-2). The MAO coatings provide superior corrosion protection for the PM 2024 aluminum alloy, and the MAO coatings obtained at a current density of 15 A dm(-2) exhibit the highest corrosion resistance.

引用

页码：1862 / 1873

页数：12

共 49 条

[21]

[蒋百灵 JIANG Bailing], 2006, [材料导报, Materials Review], V20, P155

[22]

Li S., 2001, SPEC CAST NONFERROUS, V3, P4, DOI [10.3321/j.issn:1001-2249.2001.03.002, DOI 10.3321/J.ISSN:1001-2249.2001.03.002]

[23] Influences of Additive on the Formation and Corrosion Resistance of Micro-arc Oxidation Ceramic Coatings on Aluminum Alloy [J].

Liu, Yajuan ;

Xu, Jinyong ;

Gao, Ying ;

Yuan, Ye ;

Gao, Cheng .

18TH INTERNATIONAL VACUUM CONGRESS (IVC-18), 2012, 32 :107-112

[24]

[吕伟鑫 LU Weixin], 2006, [金属热处理, Heat treatment of metals], V31, P24

[25]

[马圣林 Ma Shenglin], 2020, [表面技术, Surface Technology], V49, P104

[26] Recent advances on the antibacterial coating on titanium implant by micro-Arc oxidation process [J].

Pesode, Pralhad A. ;

Barve, Shivprakash B. .

MATERIALS TODAY-PROCEEDINGS, 2021, 47 :5652-5662

[27]

Pinliang Z., 2019, INT J IMPACT ENG, V39, P125101

[28] Performance and failure process of green recycling solutions for preparing high degradation resistance coating on biomedical magnesium alloys [J].

Qin, Jin ;

Shi, Xiaoting ;

Li, Hongyu ;

Zhao, Rongfang ;

Li, Guoqiang ;

Zhang, Shufang ;

Ding, Liyun ;

Cui, Xuejun ;

Zhao, Ying ;

Zhang, Rongfa .

GREEN CHEMISTRY, 2022, 24 (20) :8113-8130

[29]

Qun L., 2001, AM J HUM GENET, V31, P69

[30] Corrosion resistance and biocompatibility of calcium-containing coatings developed in near-neutral solutions containing phytic acid and phosphoric acid on AZ31B alloy [J].

Shi, Xiaoting ;

Wang, Yu ;

Li, Hongyu ;

Zhang, Shufang ;

Zhao, Rongfang ;

Li, Guoqiang ;

Zhang, Rongfa ;

Sheng, Yang ;

Cao, Siyue ;

Zhao, Youjun ;

Xu, Linna ;

Zhao, Ying .

JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 823

← 1 2 3 4 5 →