Fracture mechanics analysis of a closure head of a PWR reactor pressure vessel LEFM-based SIF

In this study, fracture mechanics analysis of a closure head of a PWR reactor pressure vessel has been performed under accidental conditions. For the purpose, a wide range of elliptical surface cracks starting from minute cracks to worst-case cracks was postulated at the highest stress concentration locations of the head. The analyzed accidental conditions are small break loss of coolant accident (SB-LOCA) and Rancho-Seco transient (RST). The maximum linear elastic fracture mechanics-based stress intensity factors of the worst-case crack 'a = 0.25 th; a = 0.33 c' under SB-LOCA and RST are 104.37 MPa root m and 137.12 MPa root m respectively, which are less than the fracture toughness value of the material i.e. 155.6 MPa root m. Hence, the accidental conditions do not threaten the structural integrity of the proposed closure head.