NUMERICAL ANALYSIS OF THE EFFECT OF THE REPAIR OF CORRODED PIPELINE WITH COMPOSITE PATCHES ON THE PREDICTION OF FAILURE PRESSURE

被引：0

作者：

Achira, Fouad Sodki Kara ^{[1
]}

Medjdoub, Sidi Mohamed ^{[2
]}

Hocine, Abdelkader ^{[1
]}

Dhaou, Mohamed Houcine ^{[3
]}

Chapelle, David ^{[4
]}

机构：

[1] Hassiba Benbouali Univ Chlef, Controls Lab Tests Measurements & Simulat Mech, Chlef, Algeria

[2] Univ Djillali Liabes Sidi Bel Abbes, Dept Mech Engn, Sidi Bel Abbes, Algeria

[3] Qassim Univ, Coll Sci, Dept Phys, Buraydah, Saudi Arabia

[4] Inst FEMTO ST, Dept LMARC, Besancon, France

来源：

STRUCTURAL INTEGRITY AND LIFE-INTEGRITET I VEK KONSTRUKCIJA | 2023年 / 23卷 / 01期

关键词：

corroded pipe; failure pressure; nonlinear; repair; synthetic and bio patch; stacking sequence; CORROSION DEFECTS; RELIABILITY; CRITERION; JOINT; CRACK;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The present paper focuses on the numerical prediction of failure pressure for a corroded pipeline before and after repair using composite materials patch. In the first step, the failure pressure of the corroded pipe subjected to internal pressure, has been predicted and validated using nonlinear behaviour. Then, effects of length, width and spacing of corrosion pits on failure pressure were discussed. In the second and last step, the corroded pipe is repaired with two kinds of composite patch, based on synthetic and natural fibres and the effect of reinforcement is observed. The limit of repair under increasing internal pressure is studied. The good results obtained make it possible to decide on the developed numerical model and on its reliability in predict-ing the failure pressure of corroded tubular structures and principally in optimising the thickness of the biocomposite patch repair.

引用

页码：15 / 22

页数：8

共 50 条

[31] Analytical Model and Numerical Analysis of Composite Wrap System Applied to Steel Pipeline
Djahida, Djouadi
Tewfik, Ghomari
Witek, Maciej
Abdelghani, Mechri
MATERIALS, 2021, 14 (21)
[32] Effects of Ellipsoidal Corrosion Defects on Failure Pressure of Corroded Pipelines Based on Finite Element Analysis
Zhang, J.
Liang, Z.
Han, C. J.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2015, 10 (06): : 5036 - 5047
[33] Influence of aging steel on pipeline burst pressure prediction and its impact on failure probability estimation
Gonzalez-Arevalo, N. E.
Velazquez, J. C.
Diaz-Cruz, M.
Cervantes-Tobon, A.
Teran, G.
Hernandez-Sanchez, E.
Capula-Colindres, S.
ENGINEERING FAILURE ANALYSIS, 2021, 120
[34] Experimental and numerical analysis of stability and failure of compressed composite plates
Falkowicz, Katarzyna
Ferdynus, Miroslaw
Rozylo, Patryk
COMPOSITE STRUCTURES, 2021, 263
[35] Efficient prediction method of triple failure pressure for corroded pipelines under complex loads based on a backpropagation neural network
Zhang, Tieyao
Shuai, Jian
Shuai, Yi
Hua, Luoyi
Xu, Kui
Xie, Dong
Mei, Yuan
RELIABILITY ENGINEERING & SYSTEM SAFETY, 2023, 231
[36] Reliability analysis and micromechanics: A coupled approach for composite failure prediction
Welemane, H.
Dehmous, H.
INTERNATIONAL JOURNAL OF MECHANICAL SCIENCES, 2011, 53 (11) : 935 - 945
[37] Effect of interaction between corrosion defects on failure pressure of thin wall steel pipeline
Li, Xin
Bai, Yu
Su, Chenliang
Li, Mingshu
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2016, 138 : 8 - 18
[38] Modeling of mechano-electrochemical interaction at a corrosion defect on a suspended gas pipeline and the failure pressure prediction
Qin, Guojin
Cheng, Y. Frank
THIN-WALLED STRUCTURES, 2021, 160
[39] Analysis of the adhesive thickness effect on failure pressure of metal/composite hybrid joints in pressurized blister tests
Miranda, B. M.
Reis, J. M. L.
Mattos, H. S. da Costa
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2023, 121
[40] Prediction of Failure Pressure for Defective Pipelines Reinforced with Composite System, Accounting for Pipe Extremities
S. Budhe
M. D. Banea
S. de Barros
Journal of Failure Analysis and Prevention, 2019, 19 : 1832 - 1843

← 1 2 3 4 5 →