Investigation on the hot corrosion behavior of a single crystal Ni-based superalloy in molten Na2SO4+K2SO4 salts improved by different preoxidation treatments

被引：9
作者：
Yang, Xiaowen [1 ]
Yang, Lanlan [2 ]
Wang, Jinlong [1 ]
Chen, Zehao [1 ]
Chen, Minghui [1 ]
Zhang, Jianqiang [3 ]
Wang, Fuhui [1 ]
机构：
[1] Northeastern Univ, Shenyang Natl Lab Mat Sci, Shenyang 110819, Peoples R China
[2] Jiangsu Univ Sci & Technol, Sch Mat Sci & Engn, Zhenjiang 212003, Peoples R China
[3] UNSW Sydney, Sch Mat Sci & Engn, Sydney, Australia
来源：
CORROSION SCIENCE | 2023年 / 221卷
基金：
中国国家自然科学基金;
关键词：
A; Superalloys; C; Oxidation; C. Hot corrosion; HIGH-TEMPERATURE CORROSION; OXIDATION; RESISTANCE; COATINGS; MECHANISMS; MIXTURE; TA;
D O I：
10.1016/j.corsci.2023.111377
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
This study investigated the hot corrosion behavior of N5 in molten sulfate at 850 & DEG;C after different peroxidation treatments. The preoxidation was conducted at 900, 1000 and 1100 & DEG;C for 20 and 100 h, respectively. The preformed oxide scale featured a multilayered structure and varying degrees of Ta oxides. Among all, the samples preoxidized at 900 & DEG;C exhibited the highest corrosion resistance. But a porous structure with a large number of internal oxides and sulfides was observed when preoxidized at 1000 and 1100 & DEG;C. The alloy without preoxidation directly reacted with the molten salt to form a porous structure with internal oxides and sulfides.
引用
收藏
页数：12
相关论文
共 50 条
[41]   Electrochemical study on the hot corrosion behavior of Ni16Cr13Co4Mo alloy in molten NaCl-KCl and NaCl-KCl-Na2SO4 [J].
Wang, J. H. ;
Li, D. G. ;
Shao, T. M. .
CORROSION SCIENCE, 2022, 200
[42]   Influence of Two Different Salt Mixture Combinations of Na2SO4-NaCl-NaVO3 on Hot Corrosion Behavior of Ni-Base Superalloy Nimonic263 at 800 °C [J].
Venkateswararao Mannava ;
A. SambasivaRao ;
M. Kamaraj ;
Ravi Sankar Kottada .
Journal of Materials Engineering and Performance, 2019, 28 :1077-1093
[43]   Hot corrosion behavior of APS YSZ coatings treated by laser micro glazing (LMG) under molten salts (V2O5+Na2SO4) [J].
Huo, Kun ;
Dai, Fengze ;
Qian, Wei ;
Ye, Yunxia ;
Cai, Jie ;
Hua, Yinqun ;
Zhang, Xiaofeng .
CORROSION SCIENCE, 2022, 209
[44]   Comparison investigation of hot corrosion exposed to Na2SO4 salt and oxidation of MoSi2-based coating on Nb alloy at 1000 °C [J].
Sun, Le ;
Fu, Qian-Gang ;
Sun, Jia ;
Zhang, Guang-peng .
SURFACE & COATINGS TECHNOLOGY, 2020, 385 (385)
[45]   Hot corrosion behavior of plasma-sprayed NiCr-Cr3C2-BaF2/CaF2 coatings exposed to molten Na2SO4+V2O5 and Na2SO4+NaCl at 800 oC [J].
Wu, Gensheng ;
Xie, Jianjun ;
Fang, Huanjie ;
Wang, Yongxin ;
Pu, Jibin ;
Yu, Bo ;
Ji, Li .
SURFACE & COATINGS TECHNOLOGY, 2025, 512
[46]   Corrosion behavior of HDA (hot-dip aluminized) carbon steel C45 half immersed in molten salts (NaCl, Na2SO4) isothermally at 973 K [J].
Muhammed, Hawkar J. ;
Koncz-Horvath, Daniel ;
Torok, Tamas, I .
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2023, 37 (20) :2807-2827
[47]   Hot corrosion behavior of NdYbZr2O7 exposed to V2O5 and Na2SO4 + V2O5 molten salts [J].
Wu, Yang ;
Bai, Zhiming ;
Zheng, Lei ;
He, Wenting ;
Guo, Hongbo .
CERAMICS INTERNATIONAL, 2020, 46 (07) :8543-8552
[48]   Comparative Hot Corrosion Behavior of New Nickel-Based Superalloy Ad 730 and Inconel 718 in 75 wt.% Na2SO4+25 wt.% NaCl Molten Salt Medium at 700 °C [J].
Zhou, Qihang ;
Zhang, Kaiyu ;
Zhou, Chengshuang ;
Qian, Hangli ;
Ying, Danqing ;
Li, Yuhang ;
Li, Liangliang ;
Zhang, Lin .
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025, 34 (03) :2585-2599
[49]   A study on hot corrosion performance of high velocity arc-sprayed FeCrNiAlMnB/Cr3C2 coating exposed to Na2SO4 + K2SO4 and Na2SO4 + NaCl [J].
Cheng, Jie ;
Wu, Yuping ;
Shen, Wei ;
Hong, Sheng ;
Qiao, Lei ;
Wang, Yujun .
SURFACE & COATINGS TECHNOLOGY, 2020, 397
[50]   High-Temperature Corrosion Characteristics of Ni-20Cr-xSi Alloy Laser Cladding Layer in NaCl-KCl-Na2SO4-K2SO4 Mixed Salt Environment [J].
Chen, Shanshan ;
Liu, Zongde ;
Liu, Fulai .
COATINGS, 2023, 13 (08)
12345