Extensional Rheology of Poly(vinylidene fluoride)/N,N-dimethylformamide Solutions

Typical extension flow occurs in electrospinning process of Poly(vinylidene fluoride) (PVDF) solutions such that researchers focus on extensional rheological behaviors of PVDF solutions. The extensional viscosity of PVDF solutions is measured to know the fluidic deformation in extension flows. The solutions are prepared by dissolving PVDF powder into N,N-dimethylformamide (DMF) solvent. A homemade extensional viscometric device is used to produce uniaxial extension flows and the feasibility of the viscometric device is verified by applying the glycerol as a test fluid. Experimental results show that PVDF/DMF solutions are extension shinning as well as shear shinning. The Trouton ratio of thinning PVDF/DMF solution is close to three at very low strain rate and then reaches a peak value until it drops to a small value at high strain rate. Furthermore, an exponential model may be used to fit the measured values of uniaxial extensional viscosity at various extension rates, while traditional power-law model is applicable to steady shear viscosity. For 10 similar to 14% PVDF/DMF solution, the zero-extension viscosity by fitting reaches 31.88 similar to 157.53 Pa center dot s and the peak Trouton ratio is 4.17 similar to 5.16 at applied extension rate of less than 34 s(-1). Characteristic relaxation time is lambda similar to 100 ms and corresponding critical extension rate is epsilon(c)similar to 5 s(-1). The extensional viscosity of very dilute PVDF/DMF solution at very high extension rate is beyond the limit of our homemade extensional viscometric device. This case needs a higher sensitive tensile gauge and a higher-accelerated motion mechanism for test.