Effect of moisture-heat coupling on mechanical behavior of nano-SiO2 adhesives and CFRP-steel lap joints

被引：26

作者：

Li, You ^{[1
]}

Ma, Xiaowan ^{[1
]}

Li, Hongyi ^{[1
]}

Zheng, Hui ^{[1
]}

Li, Chaunxi ^{[2
]}

Gao, Youwei ^{[2
]}

Long, Jiejie ^{[2
]}

Li, Zhaochao ^{[1
]}

机构：

[1] Hunan Univ Technol, Sch Civil Engn, Zhuzhou 412007, Hunan, Peoples R China

[2] Changsha Univ Sci & Technol, Hunan Prov Key Lab Green Construct & Maintenance B, Changsha 410114, Hunan, Peoples R China

来源：

THIN-WALLED STRUCTURES | 2023年 / 183卷

关键词：

Moisture -heat aging; Nano-SiO; 2; adhesive; CFRP-steel lap joint; Glass transition temperature; Durability; BONDED FRP/STEEL JOINTS; ENVIRONMENTAL DURABILITY;

D O I：

10.1016/j.tws.2022.110391

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

The accelerated aging tests are carried out to examine the effects of moisture-heat coupling on the mechanical properties of nano-SiO2 adhesive specimens and the bonding behavior of CFRP-steel lap joints. The microstructure of the cross-section on the failed tensile specimen is observed by scanning electron microscopy (SEM). The results indicate that the glass transition temperatures (Tg,s, Tg,t) of the adhesive decrease when the aging time of water bath increases at 25 degrees C, while the glass transition temperatures increase at 55 degrees C and 70 degrees C due to the re-curing effect of elevated temperature. Then, the shape of the stress-strain curve remains constant when the adhesive specimens take the water bath at 25 degrees C and 55 degrees C, respectively. This shape varies obviously at 70 degrees C, characterized by an obvious decreasing strength and increasing ductility, respectively. Therefore, the moistureheat temperature is recommended to be less than Tg,s for the adhesive in practical applications. Moreover, the water bath resulting in an apparent plasticization phenomenon around the pores that is the nano-SiO2 pulled out from resin matrix. In addition, the shear strength of CFRP-steel lap joint decreases because moisture-heat aging results in a decreasing bonding effect at the interfaces of CFRP-adhesive layer and steel-adhesive layer, respectively. After a water bath, the shear stress of the lap joint concentrates, and the toughness of interface decrease, resulting in a reduction of transfer length of shear stress.

引用

页数：9

共 31 条

[1] Wet thermo-mechanical behavior of steel-CFRP joints - An experimental study [J].

Agarvval, Ankit ;

Foster, Stephen J. ;

Hamed, Ehab .

COMPOSITES PART B-ENGINEERING, 2015, 83 :284-296

[2] Testing of new adhesive and CFRP laminate for steel-CFRP joints under sustained loading and temperature cycles [J].

Agarwal, Ankit ;

Foster, Stephen J. ;

Hamed, Ehab .

COMPOSITES PART B-ENGINEERING, 2016, 99 :235-247

[3]

Anni Hu, 2007, STUDY DURABILITY FRP

[4]

[Anonymous], 2018, E164018 ASTM INT

[5]

Bin Hong, 2018, STUDY WATER ALKALI S

[6]

Bo Peng, 2009, IND ARCHIT, V39, P94

[7] Effects of CNT modified adhesives and silane chemical pre-treatment on CFRP/steel bond behaviour and durability [J].

Borrie, D. ;

Al-Saadi, S. ;

Zhao, X. L. ;

Raman, R. K. Singh ;

Bai, Y. .

CONSTRUCTION AND BUILDING MATERIALS, 2021, 273

[8] Environmental durability of a CFRP system for strengthening steel structures [J].

Dawood, Mina ;

Rizkalla, Sami .

CONSTRUCTION AND BUILDING MATERIALS, 2010, 24 (09) :1682-1689

[9] Behavior of cracked steel plates strengthened with adhesively bonded CFRP laminates under fatigue Loading: Experimental and analytical study [J].

Doroudi, Y. ;

Fernando, D. ;

Hosseini, A. ;

Ghafoori, E. .

COMPOSITE STRUCTURES, 2021, 266

[10] Effect of moisture and temperature on the thermal and mechanical properties of a ductile epoxy adhesive for use in steel structures reinforced with CFRP [J].

Galvez, Pedro ;

Abenojar, Juana ;

Angel Martinez, Miguel .

COMPOSITES PART B-ENGINEERING, 2019, 176

← 1 2 3 4 →