Ultrahigh phase-transition electric field and giant energy density in NaNbO3-Bi(Zn0.5Sn0.5)O3 lead-free antiferroelectric ceramics

被引：5

作者：

Xu, Yuanjie ^{[1
]}

Xie, Aiwen ^{[1
]}

Jiang, Xuewen ^{[1
]}

Wang, Jun ^{[1
]}

Shi, Ruijian ^{[1
]}

Li, Tianyu ^{[1
]}

Xie, Xinchun ^{[1
]}

Zuo, Ruzhong ^{[1
]}

机构：

[1] Anhui Polytech Univ, Sch Mat Sci & Engn, Ctr Adv Ceram, Wuhu 241000, Peoples R China

来源：

JOURNAL OF MATERIALS CHEMISTRY C | 2023年 / 11卷 / 47期

基金：

中国国家自然科学基金;

关键词：

STORAGE DENSITY; NANBO3;

D O I：

10.1039/d3tc03815g

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Antiferroelectric (AFE) materials demonstrate great potential for dielectric energy-storage applications owing to the field-induced AFE-ferroelectric phase transition. The adjustment of the driving electric field for the phase transition (E-AF) is critical for achieving high energy-storage properties in AFEs. In this work, a complex perovskite Bi(Zr0.5Sn0.5)O-3 (BZS) with simultaneously small tolerance factor and B-site ion polarizability was introduced into NaNbO3 (NN) to form (1-x)NN-xBZS solid solutions. The results of X-ray diffraction, transmission electron microscopy and Raman spectra indicate that the room-temperature AFE orthorhombic P phase of NN can be effectively stabilized by increasing the BZS content, which is closely related to the reduced off-centering displacements of B-site cations and enhanced antiferrodistortive degree. This process is also accompanied by a reduced AFE domain size owing to the disrupted long-range AFE order. As a result, a significantly enhanced E-AF of >= 45 kV mm(-1) was realized at x = 0.06, strikingly leading to a giant recoverable energy-storage density of similar to 5.5 J cm(-3). This work makes a breakthrough progress in energy-storage performances of NN-based AFE P-phase ceramics by controlling the E-AF, which might provide a new strategy for developing AFE energy-storage materials.