Facile synthesis and characterization of magnesium and manganese mixed oxides for the efficient removal of tartrazine dye from aqueous media

Nanomaterials are the most effective class of substances for use as adsorbents in wastewater treatment. Hence, the current study involves the facile and low-cost synthesis of MgMn2O4/Mn2O3 and MgMn2O4/Mn2O3/Mg6MnO8 as novel nanostructures from mixed solutions of Mg(ii) and Mn(ii) ions using the Pechini sol-gel method. After that, the remaining powder was calcined at 500, 700, and 900 degrees C for 3 h; the products were designated as G500, G700, and G900, respectively. The G500 sample consists of MgMn2O4 and Mn2O3, while the G700 and G900 samples consist of MgMn2O4, Mg6MnO8, and Mn2O3. The synthesized nanostructures were characterized using several tools, such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and N-2 adsorption/desorption analysis. The average crystallite size of the G500, G700, and G900 samples is 210.53, 95.27, and 83.43 nm, respectively. The SEM images showed that the G500 sample consists of square and rectangular bars with an average diameter of 3.18 mu m. Also, the G700 and G900 samples consist of hexagonal, polyhedral, and irregular shapes with an average diameter of 1.12 and 0.54 mu m, respectively. The synthesized nanostructures were further utilized as adsorbents for the efficient removal of tartrazine dye from aqueous media. The experimental data showed a good fit with the Langmuir isotherm and pseudo-first-order model. The maximum adsorption capacities of the G500, G700, and G900 adsorbents toward tartrazine dye are 328.95, 359.71, and 395.26 mg g(-1), respectively.