Magnetic Properties and Microstructure of an Isothermal Annealed and Mechanically Milled Nanocrystalline Ag-Mn Alloy

The alloy 50Ag-50Mn (wt.%) was prepared using ball milling. After 50 h of milling, the samples were isothermally annealed for 1 h at a time at three different temperatures ranging from 350degree celsius to 550degree celsius. By analyzing the X-ray diffraction data, Rietveld refinement structure analysis was used to measure the lattice strain and crystallite size. The introduction of lattice strain and the decrease in crystallite size as a function of milling time may both contribute to the increase in coercivity. The analysis of superconducting quantum interference devices demonstrates the soft ferromagnetic behavior of as-milled and annealed Ag-Mn alloy. After being annealed at 350degree celsius for 1 h, the 50Ag-50Mn alloy's maximum coercivity was discovered to be 253 Oe.