Investigation of aging resistance for dental resin composites with and without glass flakes

Objectives Outstanding physical-mechanical properties and aging resistance are key requirements for dental resin composite since it will be placed in the oral environment for a long time. In this work, a new dental resin composite mainly modified by glass flakes was fabricated, and the aging resistance was evaluated by comparing with commercial composites without glass flakes.Materials and methods The new dental resin composite was produced through hand blending of inorganic glass flakes/Si-Al-borosilicate glass (58wt%:7wt% of dental resin composite), POSS-MA (5wt% of resin matrix), Bis-GMA/TEGDMA(64.4wt%:27.6wt% of resin matrix), and CQ/EDMAB (0.9wt%:2.1wt% of resin matrix) together. The flexural strength, elasticity modulus, and hardness, as well as wear were tested for evaluating the aging resistance of different dental resin composite.Results Among 6 kinds of commercial composites in this study, after 6-month water storage, the maximum percentage of performance degradation is that the flexural strength decreased 39.96%, elasticity modulus decreased 51.53% and hardness decreased 12.52%. In contrast, the new synthesized material decreased 14.53%, 20.88%, and 0.61%, respectively, and performed lesser wear depth compared to some other groups (P < 0.05).Conclusions It was observed that the new dental resin composite performed better performance stability and wear resistance when compared with commercial dimethacrylate-based or low shrinkage dental resin composite tested in this study.Clinical relevance This possibly paves a path for designing tailored dental composite for practical application. Since the aging resistance of dental resin composite modified by glass flakes is superior, it has the potential to be used for promoting the durability of dental resin composite.