Effects of scanning methods on cracking, microstructures and microhardness of Inconel 625 parts formed by direct laser metal deposition

被引:2
作者
Khoa, Tat Doan [1 ]
Le, Van Thao [2 ]
Duong, Van Nguy [1 ]
Tran, Van Chau [2 ]
机构
[1] Le Quy Don Tech Univ, Fac Mech Engn, Hanoi, Vietnam
[2] Le Quy Don Tech Univ, Adv Technol Ctr, Hanoi, Vietnam
关键词
Direct laser metal deposition; scanning method; Inconel; 625; residual stress; crack; microstructure; BEHAVIOR;
D O I
10.1051/mfreview/2024001
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
This study aims at investigating the effects of scanning methods on the stress distribution and microstructures of Inconel 625 thin-walled part fabricated by direct laser metal deposition. The results showed that with the single direction scanning (SDS) method, the residual stress at both the ends of the thin wall was relatively high while the stress at the middle was smaller with a stress difference of about 1800 MPa. In contrast, with the reverse direction scanning (RDS) method, the residual stress in the thin wall was distributed relatively evenly, with a stress difference of about 350 MPa between both the ends and the center. The experimental results showed that, in the SDS method, cracks occurred at both ends and in the middle of the thin wall, whereas in the RDS method, warping and cracks phenomena were eliminated. The microstructure of the Inconel 625 in the forming layer is characterized by a columnar crystal structure that has a small length and grows perpendicularly to the scanning direction. This growth is continuous between the forming layers. In both cases, the microhardness increases with the height of the formed layers. The microhardness values are relatively uniform with values ranging from 420 to 450 HV.
引用
收藏
页数:15
相关论文
共 15 条
[1]   Laser-aided additive manufacturing of high entropy alloys: Processes, properties, and emerging applications [J].
Arif, Zia Ullah ;
Khalid, Muhammad Yasir ;
Rehman, Ehtsham Ur .
JOURNAL OF MANUFACTURING PROCESSES, 2022, 78 :131-171
[2]  
Chena F., 2022, J. Alloys Compd, P165572
[3]   Effect of path planning on the laser powder deposition process: thermal and structural evaluation [J].
Foroozmehr, Ehsan ;
Kovacevic, Radovan .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2010, 51 (5-8) :659-669
[4]   Thermal properties of Inconel 625-NbC metal matrix composites (MMC) [J].
Grabos, Adrian ;
Rutkowski, Pawel ;
Huebner, Jan ;
Nieroda, Pawel ;
Kata, Dariusz ;
Hayashi, Shigenari .
MATERIALS & DESIGN, 2022, 224
[5]   A 3D dynamic analysis of different depositing processes used in wire arc additive manufacturing [J].
Huang, Jiankang ;
Guan, Zhichen ;
Yu, Shurong ;
Yu, Xiaoquan ;
Yuan, Wen ;
Li, Nan ;
Fan, Ding .
MATERIALS TODAY COMMUNICATIONS, 2020, 24
[6]   Investigation on cracking behavior of Ni-based coating by laser-induction hybrid cladding [J].
Huang, Yongjun ;
Zeng, Xiaoyan .
APPLIED SURFACE SCIENCE, 2010, 256 (20) :5985-5992
[7]  
Jie G., 2023, Surf. Coat. Technol, P12931
[8]   Effect of path strategy on residual stress and distortion in laser and cold metal transfer hybrid additive manufacturing [J].
Li, Runsheng ;
Wang, Guilan ;
Zhao, Xushan ;
Dai, Fusheng ;
Huang, Cheng ;
Zhang, Mingbo ;
Chen, Xi ;
Song, Hao ;
Zhang, Haiou .
ADDITIVE MANUFACTURING, 2021, 46
[9]   Effects of oxygen content on microstructure and mechanical properties of 18Ni300 maraging steel manufactured by laser directed energy deposition [J].
Li, Shihua ;
Chen, Bo ;
Tan, Caiwang ;
Song, Xiaoguo .
OPTICS AND LASER TECHNOLOGY, 2022, 153
[10]   Influence of single tensile overload on fatigue crack propagation behavior of the selective laser melting inconel 625 superalloy [J].
Ren, Duqiang ;
Xue, Zhiyuan ;
Jiang, Yun ;
Hu, Xiaoan ;
Zhang, Yu .
ENGINEERING FRACTURE MECHANICS, 2020, 239