New protective coatings against liquid zinc corrosion

被引：2

作者：

Cieplak, Aleksandra ^{[1
]}

Gdoura, Asma ^{[2
]}

Gay, Bruno ^{[3
]}

Portebois, Leo ^{[4
]}

Ramenatte, Nicolas ^{[4
]}

Proriol Serre, Ingrid ^{[1
]}

Balloy, David ^{[1
]}

机构：

[1] Univ Lille, UMR 8207, CNRS, INRAE,UMET Unite Mat & Transformat,Cent Lille, F-59000 Lille, France

[2] Carthage Univ, Natl Inst Appl Sci & Technol INSAT, BP 676, Tunis 1080, Tunisia

[3] BCircle, 2 Clos 3 Couleurs, B-1150 Brussels, Belgium

[4] Univ Lorraine, EEIGM, 6 Rue Bastien Lepage, F-54010 Nancy, France

来源：

SN APPLIED SCIENCES | 2023年 / 5卷 / 05期

关键词：

Batch galvanizing; Molten zinc corrosion; Slurry process; WT.PERCENT B STEEL; INTERFACIAL MORPHOLOGY; STAINLESS-STEEL; AL SYSTEM; BEHAVIOR; RESISTANCE; ZN;

D O I：

10.1007/s42452-023-05319-6

中图分类号：

O [数理科学和化学]; P [天文学、地球科学]; Q [生物科学]; N [自然科学总论];

学科分类号：

07 ; 0710 ; 09 ;

摘要：

Hot dip galvanizing is a surface treatment used to form a corrosion-resistant layer on the surface of steel by dipping it in a liquid zinc bath. However, a lot of structures used for hanging or containing the parts during the process are made of steel and suffer from liquid zinc corrosion. Furthermore, Fe-Zn intermetallics formed on the surface induce an additional pickling and zinc consummation, therefore generating supplementary economic and environmental costs. In this article, two Fe-Cr-Ni-Si coatings synthetized by the slurry process on carbon steel (C22) were characterized by XRD, EDX, EPMA and EBSD analyses. Their corrosion protective properties were studied in the process imitating cyclic batch galvanizing and compared to those of uncoated carbon steel (C22) and stainless steel (316 L). The coatings were verified to be more efficient than the 316 L steel usually used for this application. After 9 cycles of no weight loss, molten zinc corrosion was linear and the same for Fe-Cr-Ni-Si coatings as for the stainless steel.

引用

页数：9

共 29 条

[21] The corrosion of intermetallic alloys in liquid zinc
Wang, W. J.
Lin, J. P.
Wang, Y. L.
Chen, G. L.
[J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2007, 428 (1-2) : 237 - 243
[22] Interfacial morphology and corrosion-wear behavior of cast Fe-3.5 wt.% B steel in liquid zinc
Wang, Yong
Xing, Jiandong
Fu, Hanguang
Liu, Yangzhen
Zheng, Kaihong
Ma, Shengqiang
Jian, Yongxin
[J]. CORROSION SCIENCE, 2018, 131 : 290 - 299
[23] Interface characterization and erosion-corrosion behavior of directional Fe-3.5 wt.% B steel in flowing liquid zinc at various temperatures
Wang, Yong
Xing, Jiandong
Ma, Shengqiang
Zheng, Baochao
Liu, Guangzhu
Yang, Duoxue
Bai, Yaping
[J]. CORROSION SCIENCE, 2016, 104 : 260 - 268
[24] Interfacial morphologies and erosion-corrosion behavior of directional Fe-3.5 wt.% B steel in flowing liquid Zn containing 0.30 wt.% Al
Wang, Yong
Xing, Jiandong
Ma, Shengqiang
Zheng, Baochao
Fu, Hanguang
Liu, Guangzhu
[J]. CORROSION SCIENCE, 2016, 112 : 25 - 35
[25] Corrosion Behavior of FeB-30 wt.% Al0.25FeNiCoCr Cermet Coating in Liquid Zinc
Xie, Xiaolong
Yin, Bingbing
Yin, Fucheng
Ouyang, Xuemei
[J]. COATINGS, 2021, 11 (06)
[26] Liquid metal corrosion of 316L stainless steel, 410 stainless steel, and 1015 carbon steel in a molten zinc bath
Xu, Jing
Bright, Mark A.
Liu, Xingbo
Barbero, Ever
[J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2007, 38A (11): : 2727 - 2736
[27] Yamaguchi S, 1995, INT C ZINC ZINC ALL
[28] MoB-CoCr as alternatives to WC-12Co for stainless steel protective coating and its corrosion behavior in molten zinc
Zhang, Jifu
Deng, Chunming
Song, Jinbing
Deng, Changguang
Liu, Min
Zhou, Kesong
[J]. SURFACE & COATINGS TECHNOLOGY, 2013, 235 : 811 - 818
[29] Reaction of 316L stainless steel with a galvanizing bath
Zhang, Ke
Tang, Nai-Yong
Goodwin, Frank E.
Sexton, Scott
[J]. JOURNAL OF MATERIALS SCIENCE, 2007, 42 (23) : 9736 - 9745

← 1 2 3 →