Reversible Multimode Luminescence Modulations in Photochromic-Translucent Yb3+/Eu3+ Codoped K0.5Na0.5NbO3 Ceramics

Luminescent tunable materials have promising application potential in optical switches, optical information storage, and so on. Although europium (Eu) is a good downconversion red luminescent rare earth element, there are few studies on the upconversion luminescence and photochromism of Eu-doped potassium sodium niobate (KNN) ferroelectrics. In this paper, Eu3+ and Yb3+ codoped KNN translucent ferroelectric ceramics were synthesized and the effect of Yb3+ content on the luminescence and photochromism is studied. Both the up- and downconversion luminescence intensity and decay rate before and after photochromism can be well controlled by Yb3+ content. That is, an upconversion luminescent translucent ceramic that can be completely discolored by 405 nm light illumination for 10 s was obtained. The luminescence modulations are closely related to the evolution of oxygen vacancy and crystal field around the luminescence center, which can be verified by the illumination-induced electron paramagnetic resonance (EPR) signal and local piezoresponse switching behavior variation as well as the discovery of energy level splitting and spectral line shift. We believe that this work shows a paradigm for designing high-performance reversible multimode luminescence modulation ferroelectric ceramics.