Influence of annealing and spheroidizing treatment on microstructure and mechanical properties of AZ91 magnesium alloy

The low-strength and high-brittleness of AZ91 cast magnesium alloy mainly result from the coarse divorced eutectic phase.To solve these problems,the annealing treatment of AZ91 cast magnesium alloy was carried out at 415 ℃ and held for 24 h in this study and the alloy was then slowly cooled to room temperature in furnace.The microstructures of the alloy were observed using a metallographic microscope,a transmission electron microscopy and an emission scanning electron microscopy,respectively.The phase analysis was performed using the X-ray diffraction,and the tensile test of the specimen at ambient temperature was performed on a material test machine.The results indicate that the coarse divorced eutectic phase dissolves into the Mg matrix during the isothermal process,and the lamellar β-Mg17Al12 phase precipitates from the magnesium solid solution with a type of pearlite precipitation during furnace cooling.Consequently,the spheroidizing treatment was carried out at 320 ℃ for 20 h following the annealing process and the lamellar β-Mg17Al12 phase was spheroidized.Compared with the as-cast alloy,the strength and ductility of the AZ91 magnesium alloy are increased obviously after annealing treatment;the yield strength and tensile strength are increased to 137.8 MPa and 240.4 MPa from 102.9 MPa and 199.3 MPa,respectively;and the elongation is improved to 6.12% from 4.35%.After being spheroidized,the strength and hardness decrease a little,but the ductility is elevated to 7.23%.The nucleation,growth and spheroidizing mechanism of the lamellar β-Mg17Al12 phase were also discussed.