CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER

被引：0
|
作者：
GAO Hongbin
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1992年 / 07期
关键词：
corrosion fatigue; crack growth; crack closure; synthetic seawater;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion fatigue crack growth and near-threshold characteristics of a medium strengthsteel HT60 were investigated using compact tension specimens exposed to synthetic sea water.The da/dN-△AKrelation in air can give a conservative estimation of da/dN-△K relationsin sea water. In the case of high R, however, crack growth acceleration at high △K regionsappears to be cantrolled by the stress-assisted dissolution. The crack opening stressinlensity factor Kdetected by the back-face-strain method is the result of crack surface incontact with the corrosion products and therefore an overestimated value of Kat the cracktip is given.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [41] Effect of different loading conditions on corrosion fatigue crack growth rate of a nickel-based alloy in supercritical water
    Chen, Zhenyu
    Zhu, Zhongliang
    Wang, Bihui
    Ma, Chenhao
    Liu, Yutong
    Khan, Hasan Izhar
    Pan, Peiyuan
    Zhang, Tianyi
    Wang, Xishu
    Zhang, Naiqiang
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 175
  • [42] FATIGUE CRACK-PROPAGATION IN WELDED-JOINTS UNDER VARIABLE-AMPLITUDE LOADING IN SYNTHETIC SEA-WATER
    OHTA, A
    MAEDA, Y
    MACHIDA, S
    YOSHINARI, H
    INTERNATIONAL JOURNAL OF FATIGUE, 1990, 12 (06) : 475 - 480
  • [43] Corrosion fatigue initiation and short crack growth behaviour of austenitic stainless steels under light water reactor conditions
    Seifert, H. P.
    Ritter, S.
    Leber, H. J.
    CORROSION SCIENCE, 2012, 59 : 20 - 34
  • [44] Strength and Corrosion-Fatigue Crack-Growth Resistance of Alloys of the Ti–Nb–Zr–Si System Intended for Biomedical Purposes
    O. P. Ostash
    V. Ya. Podhurska
    B. D. Vasyliv
    L. D. Kulak
    M. M. Kuzmenko
    A. E. Fisk
    Materials Science, 2020, 55 : 648 - 655
  • [45] Crack Growth and Fatigue Strength of Deck-Rib Welded Joints in Orthotropic Steel Decks Integrating Mean Stress Effect
    Li, Xincheng
    Fu, Zhongqiu
    Ji, Bohai
    Sun, Guyu
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2025, 48 (01) : 145 - 157
  • [46] Corrosion fatigue behavior and crack-tip characteristic of 316LN stainless steel in high-temperature pressurized water
    Zhang, Ziyu
    Tan, Jibo
    Wu, Xinqiang
    Han, En-Hou
    Ke, Wei
    Rao, Jiancun
    JOURNAL OF NUCLEAR MATERIALS, 2019, 518 : 21 - 29
  • [47] Effect of oxidation behavior on the corrosion fatigue crack initiation and propagation of 316LN austenitic stainless steel in high temperature water
    Wu, H. C.
    Yang, B.
    Wang, S. L.
    Zhang, M. X.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 633 : 176 - 183
  • [48] Influence of Deposition Plane Angle and Saline Corrosion on Fatigue Crack Growth in Maraging Steel Components Produced by Laser Powder Bed Fusion
    Fernandes, Rui F.
    de Jesus, Joel
    Borrego, Luis
    Vilhena, Luis
    Ramalho, Amilcar
    Ferreira, Jose A. M.
    METALS, 2022, 12 (03)
  • [49] Corrosion-fatigue crack growth behaviour of wire arc additively manufactured ER100S-1 steel specimens
    Ermakova, Anna
    Ganguly, Supriyo
    Razavi, Nima
    Berto, Filippo
    Mehmanparast, Ali
    ENGINEERING FAILURE ANALYSIS, 2022, 138
  • [50] Corrosion fatigue crack propagation behavior of S135 high-strength drill pipe steel in H2S environment
    Liu, Ming
    Luo, Sheji
    Shen, Yi
    Lin, Xiuzhou
    ENGINEERING FAILURE ANALYSIS, 2019, 97 : 493 - 505
12345