CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER

被引：0
|
作者：
GAO Hongbin
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1992年 / 07期
关键词：
corrosion fatigue; crack growth; crack closure; synthetic seawater;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion fatigue crack growth and near-threshold characteristics of a medium strengthsteel HT60 were investigated using compact tension specimens exposed to synthetic sea water.The da/dN-△AKrelation in air can give a conservative estimation of da/dN-△K relationsin sea water. In the case of high R, however, crack growth acceleration at high △K regionsappears to be cantrolled by the stress-assisted dissolution. The crack opening stressinlensity factor Kdetected by the back-face-strain method is the result of crack surface incontact with the corrosion products and therefore an overestimated value of Kat the cracktip is given.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [31] Influence of sea water on the fatigue strength and notch sensitivity of a plasma nitrided B-Mn steel
    De la Cruz, P
    Ericsson, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 247 (1-2): : 204 - 213
  • [32] Effects of Waveform and Cycle Period on Corrosion-Fatigue Crack Growth in Cathodically Protected High-Strength Steels
    Knop, Mark
    Birbilis, Nick
    Lynch, Stan
    11TH INTERNATIONAL FATIGUE CONGRESS, PTS 1 AND 2, 2014, 891-892 : 211 - +
  • [33] Fatigue crack growth behaviour of A533B steel in pressurized water at 288 and 28°C
    Raman, SGS
    Kitsunai, Y
    ENGINEERING FAILURE ANALYSIS, 2004, 11 (03) : 293 - 303
  • [34] Corrosion fatigue crack growth behavior of pipeline steel under underload-type variable amplitude loading schemes
    Yu, Mengshan
    Xing, Xiao
    Zhang, Hao
    Zhao, Jiaxi
    Eadie, Reg
    Chen, Weixing
    Been, Jenny
    Van Boven, Greg
    Kania, Richard
    ACTA MATERIALIA, 2015, 96 : 159 - 169
  • [35] Mixed mode fatigue crack growth behavior of Ni-Cr-Mo-V high strength steel weldments
    Wang, Qiang
    Liu, Xuesong
    Wang, Wei
    Yang, Chao
    Xiong, Xiang
    Fang, Hongyuan
    INTERNATIONAL JOURNAL OF FATIGUE, 2017, 102 : 79 - 91
  • [36] Understanding the correlation of aging treatments and stress corrosion crack growth of a secondary hardening ultra-high strength steel
    Ling, Dong
    Dong, Lijin
    Wang, Hongli
    Zheng, Huaibei
    Wang, Qinying
    Liu, Li
    MATERIALS TODAY COMMUNICATIONS, 2024, 41
  • [37] Influence of sea water on the fatigue strength and notch sensitivity of a laser-hardened B-Mn steel
    De la Cruz, P
    Ericsson, T
    SCANDINAVIAN JOURNAL OF METALLURGY, 1998, 27 (01) : 2 - 13
  • [38] Effect of acetic acids on the corrosion crack growth of 3.5NiCrMoV steels in high temperature water: synergistic interaction between stress corrosion and corrosion fatigue
    Maeng, Wan Young
    INTERNATIONAL JOURNAL OF FRACTURE, 2008, 151 (02) : 217 - 231
  • [39] Effect of acetic acids on the corrosion crack growth of 3.5NiCrMoV steels in high temperature water: synergistic interaction between stress corrosion and corrosion fatigue
    Wan Young Maeng
    International Journal of Fracture, 2008, 151 : 217 - 231
  • [40] Corrosion fatigue crack growth rate for petroleum refining pressure vessel materials (2.25Cr-1 Mo steel)
    Taketomi, S.
    Yokobori, A. T., Jr.
    Takei, K.
    Wada, Y.
    Tanaka, Y.
    Iwadate, T.
    CORROSION, 2008, 64 (09) : 744 - 750
12345