CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER

被引：0
|
作者：
GAO Hongbin
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1992年 / 07期
关键词：
corrosion fatigue; crack growth; crack closure; synthetic seawater;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion fatigue crack growth and near-threshold characteristics of a medium strengthsteel HT60 were investigated using compact tension specimens exposed to synthetic sea water.The da/dN-△AKrelation in air can give a conservative estimation of da/dN-△K relationsin sea water. In the case of high R, however, crack growth acceleration at high △K regionsappears to be cantrolled by the stress-assisted dissolution. The crack opening stressinlensity factor Kdetected by the back-face-strain method is the result of crack surface incontact with the corrosion products and therefore an overestimated value of Kat the cracktip is given.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [21] Corrosion fatigue crack growth behavior of alloy 52 M in high-temperature water
    Wang, Jiamei
    Su, Haozhan
    Chen, Kai
    Du, Donghai
    Zhang, Lefu
    Sun, Yongduo
    JOURNAL OF NUCLEAR MATERIALS, 2020, 528
  • [22] Corrosion Fatigue Crack Growth Behavior of Alloy 690 in High-Temperature Pressurized Water
    Chen, Kai
    Du, Donghai
    Zhang, Lefu
    Andresen, Peter L.
    CORROSION, 2017, 73 (06) : 724 - 733
  • [23] FATIGUE CRACK-GROWTH BEHAVIOR IN WELDED-JOINTS OF HIGH-STRENGTH STEEL UNDER LOW-TEMPERATURES
    KITSUNAI, Y
    YOSHIHISA, E
    JSME INTERNATIONAL JOURNAL SERIES I-SOLID MECHANICS STRENGTH OF MATERIALS, 1991, 34 (03): : 339 - 346
  • [24] FATIGUE-CRACK GROWTH IN A HIGH-TENSILE STRENGTH STEEL IN SEAWATER AND SEVERAL OTHER ENVIRONMENTS
    OUCHI, H
    KOBAYASHI, J
    SOYA, I
    OKAMOTO, K
    ISIJ INTERNATIONAL, 1994, 34 (05) : 451 - 459
  • [25] An evaluation of fatigue crack growth in reactor steel in air and water environments considering closure effects
    Cerny, Ivo
    Linhart, Vaclav
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VI, 2007, 348-349 : 65 - +
  • [26] Effects of cycle frequency on corrosion-fatigue crack growth in cathodically protected high-strength steels
    Knop, M.
    Heath, J.
    Sterjovski, Z.
    Lynch, S. P.
    FATIGUE 2010, 2010, 2 (01): : 1243 - 1252
  • [27] Corrosion fatigue crack growth behaviour of austenitic stainless steels under light water reactor conditions
    Seifert, H. P.
    Ritter, S.
    Leber, N. J.
    CORROSION SCIENCE, 2012, 55 : 61 - 75
  • [28] EFFECTS OF MATERIAL COMPOSITION ON CORROSION FATIGUE CRACK GROWTH OF AUSTENITIC STAINLESS STEELS IN HIGH TEMPERATURE WATER
    Platts, Norman
    Tice, David
    Mottershead, Kevin
    McIntyre, Laura
    Scenini, Fabio
    15TH INTERNATIONAL CONFERENCE ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 2011, : 561 - 579
  • [29] Fatigue Crack Growth Behavior of a Mn-Ni-Cr Steel in 3.5 % NaCl Medium and Its Modeling
    Sampath, Dhinakaran
    Prakash, Raghu V.
    ADVANCES IN ELECTROCHEMICAL TECHNIQUES FOR CORROSION MONITORING AND LABORATORY CORROSION MEASUREMENTS, 2019, 1609 : 323 - 344
  • [30] Effects of heat treatment on corrosion fatigue and stress corrosion crack growth of additive-manufactured Alloy 800H in high-temperature water
    Yang, Jingfan
    Song, Miao
    Hawkins, Laura R.
    Liu, Xiang
    He, Lingfeng
    Lou, Xiaoyuan
    CORROSION SCIENCE, 2021, 191
12345