CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER

被引：0
|
作者：
GAO Hongbin
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1992年 / 07期
关键词：
corrosion fatigue; crack growth; crack closure; synthetic seawater;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion fatigue crack growth and near-threshold characteristics of a medium strengthsteel HT60 were investigated using compact tension specimens exposed to synthetic sea water.The da/dN-△AKrelation in air can give a conservative estimation of da/dN-△K relationsin sea water. In the case of high R, however, crack growth acceleration at high △K regionsappears to be cantrolled by the stress-assisted dissolution. The crack opening stressinlensity factor Kdetected by the back-face-strain method is the result of crack surface incontact with the corrosion products and therefore an overestimated value of Kat the cracktip is given.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [1] Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion
    Palin-Luc, Thierry
    Perez-Mora, Ruben
    Bathias, Claude
    Dominguez, Gonzalo
    Paris, Paul C.
    Luis Arana, Jose
    ENGINEERING FRACTURE MECHANICS, 2010, 77 (11) : 1953 - 1962
  • [2] Constraint effect of corrosion fatigue crack growth behavior in S690 high strength steel
    Han Y.
    Li Z.
    Xu L.
    Jing H.
    Zhao L.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2018, 39 (12): : 13 - 18
  • [3] EFFECIS OF TEMPERATURE AND OVERLOAD RETARDATION ON CORROSION FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL
    QIAN Yourong HE Xiangdong Beijing University of Aeronautics and Astronautics
    Acta Metallurgica Sinica(English Letters), 1990, (03) : 204 - 207
  • [4] Corrosion fatigue crack growth of AISI 4340 steel
    Weng, Lin
    Zhang, Jixi
    Kalnaus, Sergiy
    Feng, Miaoling
    Jiang, Yanyao
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 48 : 156 - 164
  • [5] Research on Corrosion Fatigue Crack Growth of Marine Engineering Equipment Material E690 High-Strength Steel
    Wang, Heng
    Liu, Xiao
    Ni, Guang-Xian
    Jiang, Jie
    SCIENCE OF ADVANCED MATERIALS, 2019, 11 (06) : 862 - 865
  • [6] An accelerated corrosion-fatigue testing method for marine high-strength steel based on equivalence principle of fatigue crack growth
    Zhang, Ruonan
    Wei, Pengyu
    Wang, Ke
    Song, Peilong
    Guo, Xin
    Zeng, Qingbo
    Li, Shengpeng
    OCEAN ENGINEERING, 2024, 314
  • [7] Very high cycle fatigue of a high strength steel under sea water corrosion: A strong corrosion and mechanical damage coupling
    Perez-Mora, Ruben
    Palin-Luc, Thierry
    Bathias, Claude
    Paris, Paul C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 74 : 156 - 165
  • [8] Evaluation of stress corrosion cracking and corrosion fatigue crack growth characteristics for martensitic stainless steel
    Inoue T.
    Sakaue K.
    Hideo C.H.O.
    Ogawa T.
    Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 2010, 76 (772): : 1698 - 1704
  • [9] Corrosion fatigue crack growth mechanisms in welded joints of marine steel structures
    Xu, Qian
    Shao, Fei
    Bai, Lin-yue
    Ma, Qing-na
    Shen, Mei
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2021, 28 (01) : 58 - 71
  • [10] Corrosion Fatigue Crack Propagation Mechanism of High-Strength Steel Bar in Various Environments
    Guo Zhongzhao
    Ma Yafei
    Wang Lei
    Zhang Jianren
    Harik, Issam E.
    JOURNAL OF MATERIALS IN CIVIL ENGINEERING, 2020, 32 (06)
12345