Fe-B-Y-Nb bulk metallic glasses in relation to clusters

被引：0

作者：

CHENG Xu1

2 Department of Mechanical Engineering

机构：

来源：

Science China(Physics,Mechanics & Astronomy) | 2008年 / 04期

基金：

中国国家自然科学基金;

关键词：

bulk metallic glass; Fe-B-Y-Nb alloys; cluster; composition design;

D O I：

暂无

中图分类号：

TG139.8 [];

学科分类号：

080502 ;

摘要：

Bulk metallic glass formations in the Fe-B-Y-Nb quaternary alloy system were in-vestigated by using the cluster line rule in combination with the minor alloying principle. The Fe-B-Y ternary system was selected as the basic system and the intersections of cluster lines were taken as the basic ternary compositions. The basic compositions were further alloyed with minor amounts of Nb. After 3-5 at.% Nb was added,the basic composition Fe68.6B25.7Y5.7,which was developed from the most densely packed cluster Fe8B3,formed 3 mm bulk metallic glasses. These quaternary bulk metallic glasses (Fe68.6B25.7Y5.7)100-xNbx (x=3-5 at.%) are expressed approximately with a unified simple composition formula: (Fe8B3)1(Y,Nb)1. The (Fe68.6B25.7Y5.7)97Nb3 bulk metallic glass has the largest glass forming ability with the following characteristic parameters Tg=907 K,Tx=1006 K,Tg/Tl=0.644,γ=0.434,and longness t=22 mm. The combination of the cluster line rule and the minor-alloying principle is a promising new route towards the quantitative composition design of multi-component metallic glasses.

引用

页码：421 / 426

页数：6

共 10 条

[1] Zr-Al-Co块状非晶的成分优化 [J].

张新房 ;

彭敏 ;

王清 ;

李德俊 ;

董闯 ;

王英敏 .

金属学报, 2004, (10) :1099-1103

[2]

Cluster-based composition rule for stable ternary quasicrystals in Al-(Cu, Pd, Ni)-TM systems[J] . C. Dong,J. B. Qiang,Y. M. Wang,N. Jiang,J. Wu,P. Thiel.Philosophical Magazine . 2006 (3-5)

[3]

Fe–Mn–Cr–Mo–(Y,Ln)–C–B (Ln = Lanthanides) bulk metallic glasses as formable amorphous steel alloys[J] . V. Ponnambalam,S. Joseph Poon,Gary J. Shiflet.Journal of Materials Research . 2004 (10)

[4]

Optimum Zr–Al–Co bulk metallic glass composition Zr 53 Al 23.5 Co 23.5[J] . X.F. Zhang,Y.M. Wang,J.B. Qiang,Q. Wang,D.H. Wang,D.J. Li,C.H. Shek,C. Dong.Intermetallics . 2004 (10)

[5]

Efficient local packing in metallic glasses[J] . D.B. Miracle.Journal of Non-Crystalline Solids . 2004 (1)

[6]

Fe-based bulk metallic glasses with diameter thickness larger than one centimeter[J] . V. Ponnambalam,S. Joseph Poon,Gary J. Shiflet.Journal of Materials Research . 2004 (5)

[7] Formation and properties of Zr48Nb8Cu14Ni12Be18 bulk metallic glass [J].

Zhang, Y ;

Zhao, DQ ;

Wang, RJ ;

Wang, WH .

ACTA MATERIALIA, 2003, 51 (07) :1971-1979

[8] A new glass-forming ability criterion for bulk metallic glasses [J].

Lu, ZP ;

Liu, CT .

ACTA MATERIALIA, 2002, 50 (13) :3501-3512

[9]

Bulk amorphous and nanocrystalline alloys with high functional properties[J] . Akihisa Inoue.Materials Science & Engineering A . 2001

[10]

Structural amorphous steels .2 Lu Z P,Liu C T,Thompson J R,et al. Physical Review Letters . 2004

← 1 →