Effects of process parameters on numerical control bending process for large diameter thin-walled aluminum alloy tubes

被引：1

作者：

李成 ^{[1
]}

杨合 ^{[1
]}

詹梅 ^{[1
]}

许旭东 ^{[2
]}

李光俊 ^{[1
]}

机构：

[1] State Key Laboratory of Solidification Processing, School of Materials Science and Engineering, Northwestern Polytechnical University

[2] Chengdu Aircraft Industry (Group) Co rporation Ltd

来源：

Transactions of Nonferrous Metals Society of China | 2009年 / 19卷 / 03期

关键词：

large diameter thin-walled aluminum alloy tubes; small bending radius; numerical control bending process;

D O I：

暂无

中图分类号：

TG146.21 [];

学科分类号：

080502 ;

摘要：

Numerical control(NC) bending experiments with different process parameters were carried out for 5052O aluminum alloy tubes with outer diameter of 70 mm, wall thickness of 1.5 mm, and centerline bending radius of 105 mm. And the effects of process parameters on tube wall thinning and cross section distortion were investigated. Meanwhile, acceptable bending of the 5052O aluminum tubes was accomplished based on the above experiments. The results show that the effects of process parameters on bending process for large diameter thin-walled aluminum alloy tubes are similar to those for small diameter thin-walled tubes, but the forming quality of the large diameter thin-walled aluminum alloy tubes is much more sensitive to the process parameters and thus it is more difficult to form.